EVALUASI SIFAT FATIK SIKLUS RENDAH BAJA TARIK DINGIN AISI 1018 YANG DILAPISI ALUMINIUM CELUP PANAS

RIO DICKY KURNIAWAN, 1345021006 (2019) EVALUASI SIFAT FATIK SIKLUS RENDAH BAJA TARIK DINGIN AISI 1018 YANG DILAPISI ALUMINIUM CELUP PANAS. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (16Kb) | Preview
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (14Mb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (14Mb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Baja tarik dingin AISI 1018 merupakan baja karbon rendah dengan kandungan karbon (C) 0.18 wt%, dan memiliki kekuatan dan keuletan yang cukup baik. Pelapisan aluminium celup panas diterapkan pada baja untuk perubahan sifat mekanik dan fatik baja. Sifat mekanik baja setelah proses pelapisan dilakukan dengan pengujian tarik (ASTM E8) dan uji fatik siklus rendah (ASTM E606) dengan amplitudo 0.003-0.005-0,007 mm/mm dan laju regangan konstan 0.005/s. Hasil pengujian tarik baja lapis aluminium menunjukan penurunan kekuatan ultimate turun sebesar 42,5 %, dan tegangan luluh turun sebesar 61,2 %. Hasil pengujian fatik siklus rendah dievaluasi menggunakan pendekatan Coffin- Manson-Basquin, untuk memprediksi umur fatik paduan dalam kondisi pembebana elastis (metode Basquin) dan plastis (metode Coffin-Mason). Perilaku pelunakan dan pengerasan regangan yang dialami pada spesimen dipelajari melalui kurva tegangan-jumlah siklus pada amplitude regangan yang diamati. Fasa intermetalik yang terbentuk dari baja tarik dingin AISI 1018 yang dilapisi Al yaitu senyawa FeAl termasuk Fe2Al5 dan FeAl3. Dan pada baja AISI 1018 yang dilapisi Al memiliki butir yang memanjang dan halus terjadi karena proses deformasi pada pengujian fatik. Kata kunci: Baja tarik dingin AISI 1018, aluminium celup panas, fatik siklus rendah, Coffin-Manson-Baquin, fasa intermetalik A cold-drawn AISI 1018 steel with a low carbon content of 0.18 wt% has high mechanical strength and is relative ductile. The steel was coated by hot-dipping aluminizing coating for the high-temperature application purposes. Regarding to application of the aluminized steel in the engineering structures, the mechanical properties and fatigue life of the materials were investigated experimentally. The mechanical and the fatigue properties of the steel with Al-coating respectively were determined by tensile testing (ASTM E8) and the low cycle fatigue tests (ASTM E606) with strain amplitude of 0.003-0.005-0,007 mm/mm at constant strain rate of 0.005/s. From the tensile test results, the ultimate strength of steel with aluminum coating decreased about 42.5% and the yield strength decreased up to about 61.2%. The properties of low cycle fatigue were determined using the Coffin-Manson-Basquin approach to predict fatigue life of steel in elastic region (Basquin equation) and plastic region (Coffin-Mason equation). The cyclic softening and hardening behavior were analyzed through a stress response with a number of cycles at the observed strain amplitude. The intermetallic phases formed on cold drawn AISI 1018 steel are Fe2Al5 and FeAl3, which decrease the low cycle fatigue life of cold-drawn ISI 1018 steel. Keywords: Cold-drawn steel

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	31 Mar 2022 10:29
Terakhir diubah:	31 Mar 2022 10:29
URI:	http://digilib.unila.ac.id/id/eprint/57070

Actions (login required)

Lihat Karya Akhir