PENGARUH MEDIA PENDINGIN QUENCHING TEMPERATUR RENDAH TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO PADA BAJA S45C

ANUGRA ARIAWAN, 1415021015 (2019) PENGARUH MEDIA PENDINGIN QUENCHING TEMPERATUR RENDAH TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO PADA BAJA S45C. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (8Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (988Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (988Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian pengaruh media pendingin quenching temperatur rendah terhadap nilai kekerasan dan struktur mikro pada baja S45C bertujuan untuk mengetahui sifat mekanis yakni nilai kekerasan dan struktur mikro dari baja. Baja S45C dipanaskan pada temperatur 850oC selama 30 menit lalu diquenching dengan menggunakan tiga media berbeda bertemperatur rendah. Media yang digunakan adalah air biasa, air garam, dan oli dengan SAE 15-40 yang bertemperatur 10oC. Proses uji kekerasan pada raw material mendapatkan nilai kekerasan sebesar 80 HRB. Untuk material yang diquenching dengan oli mendapatkan nilai 85 HRB. Untuk media quenching air biasa menghasilkan nilai kekerasan 91,73 HRB, sedangkan media air garam menghasilkan nilai kekerasan 93,6 HRB. Proses quenching dengan 3 media bertemperatur rendah tersebut menghasilkan struktur martensit pada pengamatan struktur mikro Kata kunci : Baja S45C, Quenching, Kekerasan, Struktur mikro. The study of the effect of cooling media quenching low temperature on the value of hardness and microstructure in S45C steel aims to determine the mechanical properties of the hardness and microstructure of steel. S45C steel was heated at 850oC for 30 minutes then quenched using three different medium low temperature. The media used are ordinary water, salt water, and oil with SAE 15- 40 which has a temperature of 10oC. The hardness test process on raw material gets a hardness value of 80 HRB. For materials quenched with oil get a value of 85 HRB. For ordinary water quenching media it produces a hardness value of 91.73 HRB, while brine media produces a hardness value of 93.6 HRB. The quenching process with 3 low temperature media produces a martensitic structure on the microstructure observation Keywords: S45C Steel, Quenching, Hardness, Microstructure.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	31 Mar 2022 04:13
Terakhir diubah:	31 Mar 2022 04:13
URI:	http://digilib.unila.ac.id/id/eprint/57115

Actions (login required)

Lihat Karya Akhir