ANALISIS GUGUS FUNGSI DAN SIFAT TERMAL BAHAN Li2CoSiO4 YANG DISINTESIS DARI LIMBAH KATODE BATERAI ION LITIUM DAN SILIKA SEKAM PADI

MEGAWATI, 14170410455 (2019) ANALISIS GUGUS FUNGSI DAN SIFAT TERMAL BAHAN Li2CoSiO4 YANG DISINTESIS DARI LIMBAH KATODE BATERAI ION LITIUM DAN SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK.pdf

Download (1556Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (1813Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (1814Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Studi ini bertujuan untuk mengetahui pengaruh suhu sintering terhadap gugus fungsi dan sifat termal bahan Li2CoSiO4 yang disintesis dari limbah katode baterai ion litium (BIL) dan silika sekam padi. Dekomposisi limbah katode BIL dilakukan dengan metode pelarutan asam/acid leaching dengan menambahkan Na2CO3 hingga pH 11 untuk mendapatkan senyawa Li2CO3 dan Co(OH)2 secara simultan. Ekstraksi silika sekam padi dilakukan dengan metode sol-gel. Sintesis Li2CoSiO4 dilakukan dengan metode padatan dengan perbandingan 1:1 (% berat) dan disintering dengan variasi suhu 600, 700, 800 dan 900 oC selama 12 jam. Gugus fungsi dikarakterisasi mengunakan Fourier Transform Infrared (FTIR) sedangkan sifat termal diuji menggunakan Thermo Gravimetric Analysis-Differntial Thermal Analysis (TGA-DTA). Hasil spektrum FTIR menunjukkan adanya puncak serapan yang mengindikasikan gugus fungsi dari Co-O, Li-O, Si-O-Si, Si-O-Co, Li-O-Si dan Li-O-Co. Intensitas puncak serapan mengalami peningkatan seiring suhu sintering yang semakin tinggi mengindikasikan struktur Li2CoSiO4 semakin terbentuk. Hasil TGA-DTA menunjukkan adanya penyusutan massa pada suhu 30- 400 oC yang berkaitan dengan penguapan air dan dekomposisi gugus karboksil serta penyusutan massa yang signifikan pada suhu 850-1300 oC yang berkaitan dengan kristalisasi struktur fasa γ-Li2CoSiO4. Struktur fasa γ-Li2CoSiO4 terbentuk pada suhu yang lebih rendah seiring meningkatnya suhu sintering. Sampel dengan sintering suhu 900 oC terbentuk fasa γ-Li2CoSiO4 pada suhu 1000 oC. Kata kunci: limbah baterai, sekam padi, katode Li2CoSiO4 This study aims to investigate the effect of sintering temperature on the functional groups and thermal properties of Li2CoSiO4 synthesized from lithium ion battery (LIB) cathode waste and rice husk silica. The decomposition of LIB cathode waste were synthesized by using acid leaching method by adding Na2CO3 until pH 11 to obtain Li2CO3 and Co(OH)2 compounds. Extraction of silica from rice husk were synthesized by using sol-gel method. Li2CoSiO4 were synthesized by using solid state reaction with ratio 1:1 (weight %) and sintered variation temperature at 600, 700, 800 and 900 oC for 12 hours. The functional groups were investigated using Fourier Transform Infrared (FTIR) and thermal properties using Thermo Gravimetric Analysis-Differential Thermal Analysis (TGA-DTA). The FTIR spectrum results exhibited absorption peaks which indicated the presence functional groups of Co-O, Li-O, Si-O-Si, Si-O-Co, Li-O-Si and Li-O-Co. The intensity increase with increasing sintering temperature indicated further structures Li2CoSiO4 has been formed. The TGA-DTA data exhibited weight loss at temperature range 30-400 oC due water evaporation and carbon decomposition meanwhile weight loss at temperature range 850-1300 oC due crystallization structure phase γ-Li2CoSiO4. The structure phase γ-Li2CoSiO4 formed in lower temperature with the increasing sintering temperature. The sample with sintering 900 oC was formed phase γ-Li2CoSiO4 at 1000 oC. Key words: waste battery, rice husk, Li2CoSiO4 cathode

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 01 Apr 2022 04:55
Terakhir diubah: 01 Apr 2022 04:55
URI: http://digilib.unila.ac.id/id/eprint/57313

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir