VARIASI KADAR CaCO3 TERHADAP PEMBENTUKAN FASA SUPERKONDUKTOR BSCCO-2223 MENGGUNAKAN METODE PENCAMPURAN BASAH

Prastiana Tiara Pratiwi, 151704101115 (2019) VARIASI KADAR CaCO3 TERHADAP PEMBENTUKAN FASA SUPERKONDUKTOR BSCCO-2223 MENGGUNAKAN METODE PENCAMPURAN BASAH. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (208Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2138Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2139Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mengetahui pengaruh kadar CaCO3 terhadap pembentukan fasa superkonduktor BSCCO-2223 dengan menghitung tingkat kemurnian fasa yang terbentuk, melihat stuktur mikro dan efek Meissnernya. Variasi CaCO3 yang dilakukan sebesar 1,95; 2,00; 2,05 dan 2,10 mol menggunakan metode pencampuran basah dengan suhu kalsinasi 800 °C selama 10 jam dan suhu sintering 865 °C selama 30 jam. Hasil karakterisasi XRD menunjukkan tingkat kemurnian fasa yang terbentuk meningkat seiring dengan bertambahnya kadar Ca dan optimum pada BSCCO/Ca 2,05 mol dan menurun pada BSCCO/Ca 2,10. Fraksi volume tertinggi didapatkan sebesar 74,48 % pada sampel BSCCO/Ca 2,05. Sedangkan fraksi volume terendah sebesar 48,17 % pada sampel BSCCO/Ca 1,95. Sementara, derajat orientasi tertinggi 11,61 % pada BSCCO/Ca 2,05. Derajat orientasi terendah 6,63 % pada BSCCO/Ca 1,95. Hasil karakterisasi SEM menunjukkan semua sampel telah terorientasi serta memiliki ruang kosong antar lempengan (void) yang relatif sedikit. Hasil uji efek Meissner menunnjukkan hanya pada sampel BSCCO/Ca 2,05 yang mengalami efek Meissner lemah berupa penolakan medan magnet. Kata kunci: Superkonduktor BSCCO-2223, CaCO3, fraksi volume, derajat orientasi, dan efek Meissner. This research was conducted to determine the effect of CaCO3 levels on the formation of the superconducting phase BSCCO-2223 by calculating the level of purity of the phases formed, looking at the microstructure and its Meissner effect. The variation of CaCO3 was 1.95; 2.00; 2.05 and 2.10 mole using the wet mixing method with a calcination’s temperature is 800 °C for 10 hours and a sintering’s temperature of 865 °C for 30 hours. The XRD’s chacterization results show that the level of purity of the formed phases increases with increasing Ca levels and its optimum at BSCCO/Ca 2.05 mole and then decreases at BSCCO/Ca 2.10. The highest volume fraction was 74,48 % in the BSCCO/Ca 2.05 sample. While the lowest volume fraction was 48.17 % in the BSCCO/Ca 1.95 sample. Meanwhile, the highest degree of orientation was 11.61 % at BSCCO/Ca 2.05. The lowest degree of orientation was 6.63 % at BSCCO/Ca 1.95. SEM’s chacterization results show of all samples have been oriented and have relatively little space between slabs (voids). The results of the Meissner effect show that only in the BSCCO/Ca 2.05 sample which showed a weak Meissner effect as the rejection of magnetic fields. Keywords: Superconductors BSCCO-2223, CaCO3, volume fraction, degree of orientation, and Meissner effect.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	01 Apr 2022 04:55
Terakhir diubah:	01 Apr 2022 04:55
URI:	http://digilib.unila.ac.id/id/eprint/57337

Actions (login required)

Lihat Karya Akhir