Tri Agustinus Devalo Sianipar, 1517041076 (2019) PENGARUH VARIASI La2O3 TERHADAP PRODUK Ni0,5Zn0,5LaxFe(2-x)O4. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.
|
File PDF
ABSTRAK-ABSTRACT.pdf Download (176Kb) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
File PDF
SKRIPSI FULL.pdf Restricted to Hanya staf Download (5Mb) |
|
|
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Telah dilakukan subsitusi La2O3 terhadap produk Ni0,5Zn0,5LaxFe(2-x)O4 dengan variasi x yaitu 0,010; 0,015; 0,020; 0,025; dan 0,030. Sintesis dilakukan dengan mencampurkan serbuk NiO, ZnO, La2O3, dan Fe2O3 menggunakan metode reaksi padatan. Setelah itu, sampel disinter dengan suhu 1200oC selama 5 jam. Diperoleh bahwa peningkatan substitusi La2O3 tidak mempengaruhi pembentukan fasa, yaitu menghasilkan fasa tunggal Ni0,5Zn0,5Fe2O4 (nikel zink ferrite) pada semua sampel. Tetapi mempengaruhi karakteristik produk Ni0,5Zn0,5LaxFe(2-x)O4 yaitu menghasilkan densitas yang semakin rapat. Densitas terbaik diperoleh pada sampel x=0,030 dengan kerapatan sebesar 5,351 gram/cm3 . Untuk morfologinya, substitusi La2O3 menghasilkan butiran yang semakin seragam dan mengecil. Ukuran butir yang diperoleh secara berurut yaitu 52,4 nm, 50,2 nm, 49,3 nm, 48,3 nm, dan 45,1 nm. Oleh karena peningkatan substitusi La2O3 menyebabkan densitas yang semakin rapat, serta butir yang semakin seragam dan mengecil, sehingga menghasilkan kemampuan penyerapan gelombang mikro yang semakin tinggi. Penyerapan terbaik diperoleh pada sampel x=0,030 dengan nilai penyerapan yaitu -16,17 dB dan nilai persentase penyerapan sebesar 97,58%. Kata Kunci: Ni0,5Zn0,5LaxFe(2-x)O4, Subsitusi La2O3, Penyerapan, Reaksi Padatan, dan Gelombang Mikro. Substitution La2O3 has been carried out on Ni0,5Zn0,5LaxFe(2-x)O4 products with variation x that is 0.010; 0.015; 0.020; 0.025; and 0.030. Synthesis was carried out by mixing NiO, ZnO, La2O3, and Fe2O3 powder using the solid reaction method. After that, the sample was sintered at 1200 oC for 5 hours. It was found that increasing the substitution of La2O3 did not affect the formation of the phase, ie producing a single phase Ni0,5Zn0,5Fe2O4 (nickel zinc ferrite) in all samples. But it affects the characteristics of the product Ni0,5Zn0,5LaxFe(2-x)O4, which results in denser densities. The best density was obtained in sample x = 0.030 with a density of 5,351 gram/cm3 . For morphology, the substitution of La2O3 produces increasingly uniform and smaller granules. The grain sizes obtained are sequentially 52.4 nm, 50.2 nm, 49.3 nm, 48.3 nm, and 45.1 nm. Therefore, an increase in La2O3 substitution causes densities to become denser, and granules become more uniform and smaller, resulting in higher microwave absorption capabilities. The best absorption was obtained in sample x = 0.030 with an absorption value of -16.17 dB and an absorption percentage of 97.58%. Keyword: Ni0,5Zn0,5LaxFe(2-x)O4, Substitution La2O3 , Absorption, Solid State Reaction, and Microwave.
| Jenis Karya Akhir: | Skripsi |
|---|---|
| Subyek: | 500 ilmu pengetahuan alam dan matematika > 530 Fisika |
| Program Studi: | FAKULTAS MIPA > Prodi Fisika |
| Pengguna Deposit: | UPT . Teti Novianti |
| Date Deposited: | 01 Apr 2022 04:50 |
| Terakhir diubah: | 01 Apr 2022 04:50 |
| URI: | http://digilib.unila.ac.id/id/eprint/57354 |
Actions (login required)
 |
Lihat Karya Akhir |