Desi Nurhayani, 1517041002 (2019) EFEK KONSETRASI La TERHADAP STRUKTUR DAN KARAKTERISTIK SERAPAN GELOMBANG MIKRO SISTEM MnLaXFe(2–x)O4. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (3952Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan analisis fasa sistem MnLaxFe(2-x)O4 (x = 0,010; 0,015; 0,020; dan 0,025) sebagai bahan penyerap gelombang mikro hasil sintesis dengan menggunakan metode reaksi padatan. Sistem MnLaxFe(2-x)O4 disintesis dengan mencampurkan serbuk MnO2, Fe2O3 dan La2O3 dalam perbandingan molnya dengan menggunakan metode reaksi padatan dan kemudian disintering pada suhu 1200 oC selama 5 jam. Identifikasi fasa menggunakan XRD (X-ray diffraction) menunjukkan terbentuknya fasa tunggal untuk semua komposisi mangan ferit yang didoping dengan atom La yaitu struktur spinel dengan space group Fd3m. Pengamatan morfologi dengan SEM menunjukkan bahwa penambahan atom La menyebabkan ukuran partikel antara 200-400 nm. Serapan gelombang mikro yang diukur dengan VNA (Vector Network Analyzer) menunjukkan bahwa mangan ferit yang didoping dengan atom La dapat meningkatkan kemampuan menyerap gelombang mikro dari 94.55% sampai 96.50%. Dengan demikian, komposisi x = 0,025 (MnLa0.025Fe1.975O4) merupakan komposisi terbaik yang dapat dipromosikan sebagai material baru untuk diaplikasikan sebagai bahan penyerap gelombang mikro. Kata Kunci: Mangan Ferit, Metode Reaksi Padatan, Teknik Milling, penyerapan gelombang. Phase analysis of MnLaxFe(2-x)O4 system as candidate of microwave absorber materials have been carried out. MnLaxFe(2-x)O4 (x = 0,010; 0,015; 0,020; and 0,025) using the solid reaction method. System MnLaxFe(2-x)O4 was synthesized by mixing the power MnO2, Fe2O3 and La2O3 in mole ratio using the solid state reaction method and then sintering at 1200 oC for 5 h. Phase identification with XRD (X-ray diffraction) shows that a single phase of manganese ferrite doped by lanthanum has been formed in all compositions, it has spinel structure with space group Fd3m and lattice parameter decrease with increasing x composition. Morophological observation by Scanning Electron Microscope (SEM) show that the increase of La atom the particle size of the compound powder rapidly becomes bigger, homogeneous and not uniform powder with particle size of 200-400 nm. The result of microwave a absorbing properties which measured by using VNA (Vector Network Analyzer) shows that manganese ferrite doped by lanthanum will enhance the ability to absorp microwave form 94.55% up to 96.50%. Thus, the composition of x = 0,025 (MnLa0.025Fe1.975O4) posses to be the best composition as a promising new material in microwave absorbing material application. Keywords: Manganese Ferrite, solid state reaction method, milling technique, microwave absorption

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	02 Apr 2022 22:59
Terakhir diubah:	02 Apr 2022 22:59
URI:	http://digilib.unila.ac.id/id/eprint/57446

Actions (login required)

Lihat Karya Akhir