SOFHIA CHAIRUNNISYA, 1417041087 (2019) PENGARUH TEMPERATUR DAN WAKTU REDUKSI TERHADAP PERUBAHAN FASA BIJIH MANGAN DARI NUSA TENGGARA TIMUR MENGGUNAKAN ARANG KAYU SEBAGAI REDUKTOR. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.
|
File PDF
1. ABSTRAK.pdf Download (1398Kb) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
File PDF
2. SKRIPSI FULL.pdf Restricted to Hanya staf Download (2328Kb) |
|
|
File PDF
3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf Download (1575Kb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Telah dilakukan penelitian mengenai pengaruh temperatur dan waktu reduksi terhadap perubahan fasa bijih mangan dari Nusa Tenggara Timur menggunakan arang kayu sebagai reduktor. Reduksi bijih mangan dilakukan dengan metode pirometalurgi. Pada tahap pertama dilakukan reduksi dengan variabel temperatur 900, 1000, dan 1100 °C dengan waktu reduksi dibuat tetap yaitu 15 menit. Setelah itu dilakukan proses reduksi dengan variabel waktu reduksi 30, 45, 60, dan 75 menit menggunakan temperatur terbaik yang diketahui dari tahap sebelumnya. Hasil analisis XRF menunjukkan bahwa temperatur dan waktu reduksi berpengaruh pada peningkatan kadar Mn pada bijih Mangan. Kadar Mn tertinggi mencapai 77,985 % didapatkan menggunakan temperatur 1100 °C dan waktu reduksi 45 menit. Hasil karakterisasi XRD menunjukkan bahwa raw material bijih mangan setelah direduksi mengalami perubahan fasa dan struktur mineral. Perubahan fasa yang terjadi adalah fasa pyrolusite (MnO2) menjadi fasa bixbyite (Mn2O3), braunite (Mn2SiO4) dan Hausmannite (Mn3O4). Perubahan struktur mineral yang terjadi adalah pyrolusite dan bixbyite berbentuk kubik menjadi bixbyite, braunite, dan hausmannite berbentuk tetragonal. Model kinetika yang sesuai merepresentasikan reduksi bijih Mn pada penelitian ini adalah model kinetika Ginstling-Brounshtein dengan energi aktivasi (Ea) yang didapat sebesar 9,573 kkal/mol, sehingga laju reduksi dikendalikan oleh reaksi kimia dan difusi gas. Kata Kunci : Bijih Mangan, Perubahan Fasa, Reduksi, Struktur Mineral. Effect of temperature and reduction time to phase transformation on east nusa tenggara manganese ore using charcoal as reductant has been researched. Reduction of manganese ore was carried out by pyometallurgy method. In the first step, reduction was carried out with temperature variables of 900, 1000, and 1100 °C with the reduction time being fixed at 15 minutes. After that the reduction process is carried out with the reduction time variables 30, 45, 60, and 75 minutes using the best temperature known from the previous stage. The X-Ray Fluorescence (XRF) characterization result showed that the temperature and the reduction time influeced increasing Mn content on manganese ore. The highest Mn content reaching 77.985% was obtained using a temperature 1100 ° C and a 45 minute reduction time. The X-Ray Diffraction (XRD) characterization result showed that raw material of manganese ore reduced after being reduced had transformation of phase and structure mineral. The transformation phase that occur were the pyrolusite (MnO2) phase became the bixbyite (Mn2O3), braunite (Mn2SiO4) and Hausmannite (Mn3O4) phases. The transformation in mineral structures that occur were pyrolusite and bixbyite in the form of cubic to bixbyite, braunite, and Hausmannite in the form of tetragonal.The suitable kinetic model with activation energy (Ea) obtained at 9,573 kcal / mol. The rate of reduction was controlled by chemical reaction and gas diffusion. Keywords: Manganese Ore, Phase Transformation, Reduction, Mineral Structure.
| Jenis Karya Akhir: | Skripsi |
|---|---|
| Subyek: | 500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika |
| Program Studi: | FAKULTAS MIPA > Prodi Fisika |
| Pengguna Deposit: | UPT . Teti Novianti |
| Date Deposited: | 04 Apr 2022 07:26 |
| Terakhir diubah: | 04 Apr 2022 07:26 |
| URI: | http://digilib.unila.ac.id/id/eprint/57534 |
Actions (login required)
 |
Lihat Karya Akhir |