SINTESIS DAN KARAKTERISASI DIOPSIDE DENGAN MENGGUNAKAN TEKNIK REAKSI PADATAN

Aprilia Witari Anggiyani, 1417041012 (2019) SINTESIS DAN KARAKTERISASI DIOPSIDE DENGAN MENGGUNAKAN TEKNIK REAKSI PADATAN. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
FIle PDF
ABSTRAK.pdf

Download (1381Kb) | Preview
[img] FIle PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (1669Kb)
[img]
Preview
FIle PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (1670Kb) | Preview

Abstrak

Diopside telah berhasil disintesis dengan menggunakan teknik reaksi padatan, yang kemudian disintering pada suhu 900 oC, 1000 oC, 1100 oC, dan 1200 oC. Diopside dikarakterisasi menggunakan DTA-TGA, XRD, FTIR, dan SEM-EDX. Hasil DTA memperlihatkan adanya transisi keramik kaca CaO-MgO-2SiO2 pada suhu 692 oC, dan adanya puncak eksotermik pada suhu 880 oC yang menandai proses kristalisasi pada sampel. Sedangkan hasil TGA menunjukan total penyusutan massa sebesar 21,47 % dari massa awal. Analisis XRD menunjukan adanya fase diopside pada semua suhu sintering sebagai fase utama dengan intensitas tertinggi pada 2θ sebesar 29,9 o . Spektrum FTIR pada semua sampel memperlihatkan adanya ikatan O-Ca-O, O-Mg-O, O-Si-O dan Si-O yang mengindikasi terbentuknya diopside. Morfologi SEM menunjukan permukaan sampel berbentuk gumpalan yang tidak teratur, dan ukuran partikel diopside semakin mengecil dengan meningkatnya suhu sintering. Sedangkan hasil EDX menunjukan unsur yang terdapat pada sampel yaitu Ca, Mg, Si, dan O. Kata kunci: Diopside, biomaterial, sistem CaO-MgO-SiO2, reaksi padatan. Diopside has been successfully synthesized using solid reaction techniques, which are then sintered at temperatures of 900 oC, 1000 oC, 1100 oC, and 1200 oC. Diopside was characterized using DTA-TGA, XRD, FTIR, and SEM-EDX. The DTA results showed a transition of CaO-MgO-2SiO2 glass ceramics at a temperature of 692 oC, and the presence of exothermic peaks at 880 oC which marked the crystallization process in the sample. While the TGA results show total mass shrinkage of 21.47 % of the initial mass. XRD analysis shows the diopside phase at all sintering temperatures as the main phase with the highest intensity at 2θ at 29.9o . The FTIR spectrum in all samples shows the presence of O-Ca-O, O-Mg-O, O-Si-O, and Si-O bonds which indicate diopside formation. SEM morphology shows that the sample surface is agglomerate and irregular shapes, and the size of the diopside particles decreases with increasing sintering temperature. While the EDX results show the elements found in the sample are Ca, Mg, Si, and O. Keywords: Diopside, biomaterial, CaO-MgO-SiO2 system, solid reaction.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi: Fakultas MIPA > Prodi Fisika
Pengguna Deposit: UPT . Teti Novianti
Date Deposited: 02 Apr 2022 22:45
Terakhir diubah: 02 Apr 2022 22:45
URI: http://digilib.unila.ac.id/id/eprint/57559

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir