PENGARUH KONSENTRASI PERAK NITRAT (0,3; 0,5; 0,7 M) TERHADAP FUNGSIONALITAS, STRUKTUR, DAN DENSITAS KOMPOSIT PERAK SILIKA Ag/SiO2

JANARIAH, 1717041002 (2022) PENGARUH KONSENTRASI PERAK NITRAT (0,3; 0,5; 0,7 M) TERHADAP FUNGSIONALITAS, STRUKTUR, DAN DENSITAS KOMPOSIT PERAK SILIKA Ag/SiO2. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (375Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2914Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2610Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian mengenai sintesis komposit perak silika (Ag/SiO2) telah dilakukan menggunakan metode sol-gel dengan variasi konsentrasi sol perak nitrat (AgNO3) sebesar 0,3; 0,5 dan 0,7 M ke dalam sol silika sekam padi dan diberi perlakuan termal suhu 110 oC dan suhu sintering 850 oC. Tujuan dari penelitian ini yaitu untuk mengetahui gugus fungsi, struktur dan uji nilai densitas komposit Ag/SiO2. Karakterisasi gugus fungsi menggunakan FTIR diperoleh puncak serapan Si-OH, Si-O-Si, dan Si-O sebagai tanda keberadaan silika pada sampel dengan pergeseran pita serapan akibat penambahan konsentrasi AgNO3. Karakterisasi struktur menggunakan XRD menunjukkan adanya struktur silika amorf dan struktur kristal kubik perak (face center cubic, FCC) pada konsentrasi 0,3 M, penambahan konsentrasi 0,5 dan 0,7 M mempengaruhi kenaikan intensitas 2θ pada struktur perak dan membentuk struktur silika kristobalit. Uji nilai densitas menggunakan metode Archimedes menghasilkan nilai secara berturut-turut sebesar 1,75; 1,89 dan 1,98 g/cm3. Kata kunci: Ag/SiO2, AgNO3 (0,3; 0,5; 0,7 M); densitas, gugus fungsi, silika sekam padi; struktur kristal. ABSTRACT Research on the synthesis of silver silica (Ag/SiO2) composites has been carried out using the sol-gel method with variations concentration of sol silver nitrate (AgNO3) of 0.3; 0.5 and 0.7 M into the silica sol of rice husk and given thermal treatment at 110 oC and sintering 850 oC. The purpose of this research is to know of functional groups, structure, and the density value of Ag/SiO2 composites. The characterization of functional groups using FTIR obtained absorption peaks of Si-OH, Si-O-Si, and Si-O as a sign of the presence of silica in the sample with a shift in the absorption band due to the addition of AgNO3. The structural characterization using XRD showed the presence of amorphous silica structure and cubic crystal structure of silver (face center cubic, FCC) at a concentration of 0.3 M, the addition of 0.5 and 0.7 M concentrations affected the 2θ intensity increase in the silver structure and formed a silica cristobalite structure. The density test using the Archimedes method resulted value of 1.75; 1.89 and 1.98 g/cm3. Keywords: Ag/SiO2, AgNO3 (0.3; 0.5; 0.7 M); density, functional group, rice husk silica; crystal structure.

Jenis Karya Akhir:	Skripsi
Subyek:	000 Ilmu komputer, informasi dan pekerjaan umum 500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2203910928 . Digilib
Date Deposited:	01 Apr 2022 04:35
Terakhir diubah:	01 Apr 2022 04:35
URI:	http://digilib.unila.ac.id/id/eprint/57614

Actions (login required)

Lihat Karya Akhir