PENGARUH VARIABEL KINETIS TERHADAP EFEKTIVITAS REAKSI TRANSESTERIFIKASI MINYAK BIJI KARET MENGGUNAKAN KATALIS NiO/ZEOLIT-Y

ROSALINDA YULIANI, 1717011061 (2022) PENGARUH VARIABEL KINETIS TERHADAP EFEKTIVITAS REAKSI TRANSESTERIFIKASI MINYAK BIJI KARET MENGGUNAKAN KATALIS NiO/ZEOLIT-Y. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK.pdf

Download (4013Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (4013Kb)
[img]
Preview
File PDF
SKRIPSI TANPA PEMBAHASAN.pdf

Download (4013Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini, komposit NiO/zeolit-Y disintesis menggunakan metode impregnasi dengan memvariasikan komposisi logam NiO terhadap zeolit-Y yakni 0, 5, 10, 15 dan 20%. Komposit NiO/zeolit-Y selanjutnya digunakan sebagai katalis pada reaksi transesterifikasi minyak biji karet dengan metanol. Penelitian diawali dengan mensintesis zeolit-Y menggunakan metode hidrotermal dengan memanfaatkan silika sekam padi dan alumunium foil food gradesebagai bahan baku. Metode hidrotermal dilakukan pada suhu kristalisasi 100ºC selama 48 jam kemudian diikuti dengan proseskalsinasi pada suhu 550ºC selama 6 jam. Komposit NiO/zeolit-Y dan zeolit-Y dikarakterisasi menggunakan XRD, SEM dan FTIR. Hasil karakterisasi XRD zeolit-Y menunjukkan adanya kemiripan dengandatabase standar IZA. Morfologi permukaan zeolit-Y berbentuk bulat dengan karakteristik bentuk lingkaran yang tersusun dari kumpulan balok-balok kristal yang tumbuh mencuat dari pusat lingkaran. Impregnasi oksida NiO pada zeoit-Y tidak merubah dan merusak struktur pada zeolit-Y dibuktikan dengan dipertahankannya karakteristik bentuk bulat pada kristal. Penggunaan komposit NiO/zeolit-Y sebagai katalis pada reaksi transesterifikasi menunjukkan aktivitas katalitik yang baik. Komposit NiO/zeolit-Y dengan kandungan logam 20% memiliki aktivitas katalitik terbaik, dengan tingkat konversi minyak biji karet menjadi biodiesel yang tercapai sebesar 89%. Karakterisasi GC-MS menunjukkan bahwa produk transesterifikasi terdiri dari campuran metil ester yang sesuai dengan kandungan asam lemak dalam minyak biji karet dengan komposisi utamanya adalah metil linoleat sebesar 39,59%. Kata Kunci: zeolit-Y, komposit NiO/zeolit-Y, katalis, transesterifikasi, minyak biji karet. In this study, NiO/zeolite-Y composites were synthesized using the impregnation method by varying the metal composition of NiO to zeolite-Y, namely 0, 5, 10, 15, and 20%. The NiO/zeolite-Y composites were used as a catalyst in the transesterification reaction of rubber seed oil with methanol. The research was initiated by synthesizing zeolite-Y using the hydrothermal method by utilizing rice husk silica and food-grade aluminum foil as raw materials. The hydrothermal method was conducted at a crystallization temperature of 100ºC for 48 hours and then calcined at 550ºC for 6 hours. NiO/zeolite-Y composite and zeolite-Y were characterized using XRD, SEM, and FTIR. The results of the XRD zeolite-Y characterization showed similarities with the IZA standard database. The surface morphology of the zeolite-Y is round with a characteristic circular shape composed of collection of crystal blocks that grow sticking out from the center of the circle. NiO oxide impregnation in zeolite-Y did not change and damage the structure of zeolite-Y as evidenced by the preservation of the characteristic round shape of the crystal. Using NiO/zeolite-Y composite as a catalyst in the transesterification reaction showed good catalytic activity. NiO/zeolite-Y composite with 20% nickel content had the best catalytic activity, with the conversion rate of rubber seed oil into biodiesel achieved at 89%. GC-MS characterization showed that the transesterification product consisted of a mixture of methyl esters which matched the fatty acid content in rubber seed oil with 39,59% methyl linoleate as the main composition. Keyword: zeolite-Y, NiO/zeolite-Y composite, catalyst, transesterification, rubber seed oil

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
600 Teknologi (ilmu terapan) > 660 Teknik kimia
Program Studi: FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit: 2203593602 1717011061 Rosalinda Yuliani
Date Deposited: 27 Apr 2022 03:00
Terakhir diubah: 27 Apr 2022 03:00
URI: http://digilib.unila.ac.id/id/eprint/60568

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir