ALKANOLAMIDA BERBASIS MINYAK BIJI KARET (Hevea brasiliensis) SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2)

MUTIARA NUR AULIA, 1617011035 (2021) ALKANOLAMIDA BERBASIS MINYAK BIJI KARET (Hevea brasiliensis) SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Mutiara Nur Aulia.pdf Download (3050Kb) | Preview
	File PDF FULL SKRIPSI (Tanpa Lampiran Isi) - Mutiara Nur Aulia.pdf Restricted to Hanya staf Download (3698Kb)
Preview	File PDF FULL SKRIPSI TANPA BAB PEMBAHASAN (Tanpa Lampiran Isi) - Mutiara Nur Aulia.pdf Download (3698Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini, dipelajari aktivitas inhibitor produk amidasi metil ester minyak biji karet dengan menggunakan zeolit A berbasis sekam padi sebagai katalis. Hasil sintesis zeolit A terkonfirmasi melalui XRD dan SEM-EDS. Transesterifikasi minyak biji karet dilakukan pada suhu 70°C selama 6 jam dan produk dikarakterisasi menggunakan FTIR dan GC-MS. Amidasi dilakukan dengan mereaksikan metil ester yang diperoleh dari transesterifikasi dengan dietanolamina dan dikarakterisasi menggunakan FTIR dan GC-MS. Produk amidasi diuji aktivitasnya sebagai inhibitor korosi baja lunak dalam medium NaCl 3% jenuh CO2 menggunakan metode Wheel test dan metode elektrokimia (EIS dan Tafel). Hasil penelitian menunjukkan bahwa zeolit A mempunyai aktivitas yang baik sebagai katalis untuk transesterifikasi, tetapi tidak untuk amidasi. Uji aktivitas inhibitor korosi menunjukkan bahwa produk amidasi pada konsentrasi 150 mg.L-1 dan suhu 50°C menghasilkan proteksi sebesar 52,00% berdasarkan metode Wheel test, 88,44% berdasarkan metode EIS, dan 74,12% berdasarkan metode Tafel. Kemampuan produk amidasi sebagai inhibitor korosi juga ditunjukkan oleh morfologi permukaan seperti yang ditampilkan hasil analisis menggunakan SEM dari sampel baja lunak yang diteliti. Kata kunci: Zeolit A, minyak biji karet, transesterifikasi, amidasi, baja lunak, inhibitor korosi. In this research, the inhibitor activity of rubber seed oil methyl ester amidation product using zeolite A as catalyst was studied based. The zeolite was synthesized from rice husk silica and aluminum foil as raw materials, and confirmed by XRD and SEM-EDS. Transesterification of rubber seed oil was carried out at 70°C for 6 hours, and the product was analyzed using FTIR and GC-MS technique. Amidation was attempted by reacting the methyl esters obtained from transesterification with diethanolamine and the product was analyzed using FTIR and GC-MS. The amidation product was then tested as a corrosion inhibitor of mild steel in CO2 saturated 3% NaCl medium using the Wheel test method and the electrochemical method (EIS and Tafel). The experimental results indicate that zeolite A has high activity as catalyst for transesterification, but not for amidation. Corrosion inhibition experiments revealed that the amidation product at a concentration of 150 mg.L-1 and a temperature of 50°C resulted in 52.00% protection based on the Wheel test, 88.44% based on the EIS method, and 74.12% based on the Tafel method. The ability of the amidati on product to act as corrosion inhibitor is also demonstrated by the surface morphology of the sample as displayed by SEM image of the mild steel sample investigated. Keywords: Zeolite A, rubber seed oil, transesterification, amidation, mild steel, corrosion inhibitor.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	28 Apr 2022 07:39
Terakhir diubah:	28 Apr 2022 07:39
URI:	http://digilib.unila.ac.id/id/eprint/60653

Actions (login required)

Lihat Karya Akhir