KARAKTERISTIK STRUKTUR DAN TERMAL ASPAL-KARBOSIL KOMPOSIT

LIYANA MARDOVA, 1927041007 (2021) KARAKTERISTIK STRUKTUR DAN TERMAL ASPAL-KARBOSIL KOMPOSIT. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - liyana mardova.pdf Download (1167Kb) | Preview
	File PDF TESIS FULL - liyana mardova.pdf Restricted to Hanya staf Download (1544Kb)
Preview	File PDF TESIS TANPA BAB PEMBAHASAN - liyana mardova.pdf Download (1545Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada penelitian ini dilakukan karakterisasi komposit aspal karbosil dengan variasi komposisi aspal karbosil yaitu 1:9; 1,5:8,5; 2:8; 2,5:7,5; 3:7 dan perbandingan untuk karbosil murni tanpa penambahan aspal. Karbosil didapatkan dari limbah sekam padi dengan menggunakan metode pirolisis. Penelitian ini dilakukan untuk mengetahui pengaruh struktur dan termal komposit aspal karbosil. Hasil Analisis XRD terbentuk dari setiap variasi komposisi adalah fasa amorf. Analisis DTA/TGA menunjukkan terjadinya perubahan energi akibat penambahan panas dengan ditandai adanya penyusustan massa pada sampel. Hasil uji meknik kuat tekan menunjukkan bahwa kekuatan komposit aspal karbosil dengan berbeda komposisi bahan mempengaruhi ketahanan terhadap keretakan. Hasil uji fisis porositas dan perubahan ketebalan menunjukkan dengan penambahan variasi komposisi aspal dan karbosil mengakibatkan menurunnya nilai porositas dan perubahan ketebalan. Uji mekanik dan fisis perbandingan aspal karbosil yang baik adalah pada perbandingan komposisi 3:7 pada komposis tersebut memiliki porositas dan perubahan ketebalan yang paling kecil sehingga lebih tahan retakan sesuai dengan hasil uji kuatkan yaitu sebesar 18,408 N/mm2 . Kata kunci: karbosil, aspal, pirolisis, XRD, dan DTA/TGA. In this study, the characterization of the carbosil asphalt composite was carried out with variations in the composition of the carbosil asphalt, namely 1:9; 1.5:8.5; 2:8; 2.5:7.5; 3:7 and the ratio for pure carbosil without the addition of asphalt. Carbosil was obtained from rice husk waste by using the pyrolysis method. This research was conducted to determine the structural and thermal effects of carbosil asphalt composites. The results of XRD analysis formed from each variation of the composition was an amorphous phase. The DTA/TGA analysis shows that there is a change in energy due to the addition of heat, which indicated by the presence of mass shrinkage in the sample. The results of the mechanical compressive strength test show that the strength of the carbosil asphalt composite with different material compositions affects the resistance to cracking. The results of the physical test of porosity and changes in thickness showed that the addition of variations in the composition of asphalt and carbosil resulted in a decrease in the value of porosity and changes in thickness. The mechanical and physical test of a good ratio of carbosil asphalt is that the composition ratio of 3:7 in the composition has the smallest porosity and thickness changes so that it is more resistant to cracking according to the results of the reinforcement test, which is 18.408 N/mm2 . Keywords: carbosil, asphalt, pyrolysis, XRD, and DTA/TGA.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Magister Ilmu Fisika
Pengguna Deposit:	UPT . Rukiah
Date Deposited:	12 May 2022 04:23
Terakhir diubah:	12 May 2022 04:23
URI:	http://digilib.unila.ac.id/id/eprint/60944

Actions (login required)

Lihat Karya Akhir