FABRIKASI POROUS MAGNESIUMBERPORI PADA KONDISI SEMISOLID MENGGUNAKANTITANIUM WIRE SPACE HOLDER (TWSH) SEBAGAI MATERIALBIODEGRADABLE BONE SCAFFOLD

Ulin Herlina, 1925021002 (2021) FABRIKASI POROUS MAGNESIUMBERPORI PADA KONDISI SEMISOLID MENGGUNAKANTITANIUM WIRE SPACE HOLDER (TWSH) SEBAGAI MATERIALBIODEGRADABLE BONE SCAFFOLD. Masters thesis, Universitas Lampung.

Preview	File PDF Abstrak Ulin Herlina - Ulin Herlina.pdf Download (4Mb) | Preview
	File PDF Thesis Ulin Herlina 12 Agt 2021 lengkap tanpa lampiran - Ulin Herlina.pdf Restricted to Hanya staf Download (5Mb)
Preview	File PDF Thesis tanpa pembahasan Ulin Herlina 12 Agt 2021 revisi 14 Agustus 2021 - Ulin Herlina.pdf Download (5Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Magnesium berpori merupakan salah satu material yang dapat dijadikan impant tulang yang berbentuk bulk(scaffold) karena dapat digunakan pada jaringan tubuh manusia dan bersifat biodegradable, non-toxic serta menyerupai tulang alami. Bentuk pori pada magnesium dengan interkonesi yang menyerupai tulang asli merupakan tantangan tersendiri pada pabrikasi pembuatan magnesium berpori untuk material bone scaffold. Oleh karena itu dilakukan kegiatan penelitian pembuatan magnesium berpori menggunakan Titanium Wire Space Holder (TWSH) dengan proses semi solid untuk menghasilkan material bone scaffoldyang biodegradable. Proses yang dilakukan pada penelitian ini adalah dengan melakukan kompaksi dan sintering material magnesium serbuk dengan titanium wire menggunakan alat squeeze casting pada proses semi-solid, kemudian dilarutkan menggunakan larutan asam hydro fluoride agar terbentuk porous magnesium. Pengujian yang dilakukan adalah laju korosi, densitas dan poritas, kekerasan dan SEM-EDX. Penelitian ini berhasil melakukan fabrikasi porousmagnesium yang berpotensi sebagai bahan material bone scaffold dimana variasi bahan uji yang mendekati sifat tulang adalah specimen dengan suhu sintering 570°C komposisi Ti:Mg = 2:3. Kata Kunci : porousmagnesium, squeeze casting, bone scaffold, titanium wire ii Porous magnesium is one of the materials that can be used as bone implants in bulk (scaffold) because it can be used in human body tissues and is biodegradable, non-toxic and resembles natural bone. The pore shape of magnesium with interconnections that resemble natural bone is a challenge in fabricating porous magnesium for bone scaffold material. Therefore, research activities were carried out to fabricate porous magnesium using a Titanium Wire Space Holder (TWSH) with a semi-solid process to produce biodegradable bone scaffold material. The process carried out in this research is by compacting and sintering magnesium powder material with titanium wire using a squeeze casting tool in a semi-solid process, then dissolved using a hydrofluoric acid solution to form porous magnesium. The tests carried out were corrosion rate, density and porosity, hardness and SEM-EDX. This study succeeded in fabricating porous magnesium, which has the potential as a bone scaffold material where the variation of the test material that is close to bone properties is a specimen with a sintering temperature of 570°C with a composition of Ti : Mg = 2:3. Keywords: porousmagnesium, squeeze casting, bone scaffold, titanium wire

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi Magister Teknik Mesin
Pengguna Deposit:	UPT Anita Ekarini
Date Deposited:	20 May 2022 07:45
Terakhir diubah:	20 May 2022 07:45
URI:	http://digilib.unila.ac.id/id/eprint/61430

Actions (login required)

Lihat Karya Akhir