SINTESIS DAN KARAKTERISASI WOLLASTONITE BERBASIS PREKUSOR BIOGENIK SILIKA ABU SEKAM PADI

Amilia Rasitiani, 1827041006 (2021) SINTESIS DAN KARAKTERISASI WOLLASTONITE BERBASIS PREKUSOR BIOGENIK SILIKA ABU SEKAM PADI. Masters thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Amilia Rasitiani.pdf Download (2082Kb) | Preview
	File PDF TESIS FULL - Amilia Rasitiani.pdf Restricted to Hanya staf Download (2543Kb)
Preview	File PDF TESIS TANPA BAB PEMBAHASAN - Amilia Rasitiani.pdf Download (2544Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sintesis wollastonite telah dilakukan dengan bahan dasar silika sekam padi dan kalsium karbonat komersil. Perubahan reaksi kimia, fasa, gugus fungsi, dan morfologi wollastonite dipengaruhi oleh suhu kalsinasi 900 oC, 1000 oC, dan 1100 oC. Hasil DTA-TGA menunjukkan penyusutan massa karena terjadinya penguapan H2O dan dekomposisi CaCO3 menjadi CaO seiring meningkatnya suhu kalsinasi, selain itu, hasil DTA juga mengidentifikasi adanya pembentukan fasa β- CaSiO3 dan fasa α-CaSiO3. Berdasarkan hasil XRD, wollastonite yang didapatkan didominasi oleh fasa β-CaSiO3 dan fasa minor adalah α-CaSiO3 hal ini ditunjukkan oleh puncak intensitas fasa β-CaSiO3 lebih tinggi dibandingkan puncak intensitas fasa α-CaSiO3. Pembentukan kedua fasa tersebut dalam wollastonite juga diperkuat dari hasil FTIR melalui analisis gugus fungsi Si-O-Ca pada setiap sampel wollastonite. Selain itu, hasil analisa SEM menunjukkan bentuk partikel spheroid (bulat) dengan ukuran butir rata-rata 0,19 μm, 0,35 μm dan 0,68 μm untuk masing-masing suhu kalsinasi 900 oC, 1000 oC dan 1100 oC. Hasil penelitian ini menunjukkan bahwa pembuatan wollastonite dari bahan dasar silika sekam padi dan kalsium karbonat komersil mempunyai potensi sebagai bahan alternatif pembuatan wollastonite. Kata kunci: sekam padi, kalsium karbonat, wollastonite, metode reaksi padatan. Wollastonite was synthesized with the basic ingredients of rice husk silica and commercial calcium carbonate. Changes in chemical reactions, phases, functional groups, and morphology of wollastonite are affected by calcination temperatures of 900 oC, 1000 oC, and 1100 oC. The results of DTA-TGA showed mass shrinkage due to the evaporation of H2O and the decomposition of CaCO3 into CaO as the calcination temperature increased. In addition, the results of DTA also identifies the formation of β-CaSiO3 and α-CaSiO3 phases. Based on the XRD results obtained wollastonite is dominated by the β-CaSiO3 phase and the minor phase is α-CaSiO3 this is indicated by the peak intensity of the β-CaSiO3 phase which is higher than the peak intensity of the α-CaSiO3 phase. The formation of these two phases in wollastonite is also confirmed from the FTIR results through the analysis of the Si-O-Ca functional group in each wollastonite sample. In addition, the results of the SEM analysis shows the shape of the spheroidal particles (spherical) with an average grain size of 0.19 μm, 0.35 μm and 0.68 μm for the calcination temperatures of 900 oC, 1000 oC and 1100 oC, respectively. The results of this study indicate that the manufacture of wollastonite from rice husk silica and commercial calcium carbonate has potential as an alternative material for the manufacture of wollastonite. Keywords: rice husk, calcium carbonate, wollastonite,solid state reaction.

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	500 ilmu pengetahuan alam dan matematika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	UPT . Neti Yuliawati
Date Deposited:	24 May 2022 07:18
Terakhir diubah:	24 May 2022 07:18
URI:	http://digilib.unila.ac.id/id/eprint/61750

Actions (login required)

Lihat Karya Akhir