ANALISIS EFEKTIVITAS CAMPURAN METIL ESTER TURUNAN MINYAK KELAPA SAWIT (Elaeis guineensis jacq) DENGAN DIETANOLAMINA SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2)

Apri Dearni Sinaga, 1717011083 (2021) ANALISIS EFEKTIVITAS CAMPURAN METIL ESTER TURUNAN MINYAK KELAPA SAWIT (Elaeis guineensis jacq) DENGAN DIETANOLAMINA SEBAGAI INHIBITOR KOROSI BAJA LUNAK DALAM MEDIUM YANG MENGANDUNG KARBON DIOKSIDA (CO2). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK - Apri Dearni.pdf

Download (1972Kb) | Preview
[img] File PDF
SKRIPSI FULL - Apri Dearni.pdf
Restricted to Hanya staf

Download (2441Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN - Apri Dearni.pdf

Download (2442Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Korosi merupakan masalah besar yang dihadapi dunia sehingga membutuhkan penanganan yang serius. Inhibitor korosi menjadi salah satu cara efektif untuk mencegah terjadinya korosi karena pembuatannya yang mudah dan ramah lingkungan. Penelitian ini dilakukan untuk menguji efikasi campuran dietanolamina dan metil ester turunan minyak kelapa sawit sebagai inhibitor korosi baja lunak dalam larutan garam yang mengandung CO2. Metil ester dibuat dengan transesterifikasi minyak kelapa sawit menggunakan metanol dengan katalis zeolit-A. Serangkaian campuran dibuat dengan mencampur dietanolamin dan metil ester dengan perbandingan yaitu 0:5; 1:4; 2:3; 3:2; 4:1; dan 5:0. Uji inhibitor korosi dilakukan dalam larutan NaCl 3% dengan CO2 menggunakan metode wheel test, dan morfologi atau sampel logam dianalisis menggunakan SEM (Scanning Electron Microscopy). Hasil yang diperoleh menunjukkan bahwa persentasi proteksi tertinggi sebesar 58,23% diperoleh dari percobaan menggunakan larutan inhibitor dengan perbandingan dietanolamin terhadap metil ester 3:2. Proteksi inhibitor juga ditunjukkan oleh morfologi permukaan sampel yang dilihat dengan SEM. Kata Kunci: Inhibitor korosi, baja lunak, metil ester minyak kelapa sawit, wheel test. Corrosion is a big problem facing the world that requires serious handling. Corrosion inhibitors is one of the effective ways to prevent corrosion because they are easy to manufacture and environmentally friendly. This research was conducted to test the efficacy of mixed diethanolamine and palm oil-derived methyl esters as corrosion inhibitor of mild steel in CO2 containing brine solution. Methyl esters were prepared by transesterification of palm oil using methanol in the presence of zeolite-A as catalyst. A series of mixtures were prepared by mixing diethanolamine and methyl esters with the ratios of 0:5; 1:4; 2:3; 3:2; 4:1; and 5:0. Corrosion inhibition experiments were conducted in a 3% NaCl solution with CO2 using wheel test method, and the morphology of the metal sample was analysed using SEM (Scanning Electron Microscopy). The results obtained indicate that the highest percent of protection of 58.23 % was obtained from the experiment using the inhibitor solution with the ratio of diethanolamin to methyl esters of 3:2. The protection of the inhibitor was also indicated by surface morphology of the sample as seen by SEM. Keywords: Corrosion inhibitor, mild steel, palm oil methyl ester, wheel test.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi: FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit: AM.d Firlia Hidayah
Date Deposited: 30 Aug 2022 13:16
Terakhir diubah: 30 Aug 2022 13:16
URI: http://digilib.unila.ac.id/id/eprint/65878

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir