ANALISIS PERTUMBUHAN FASE SUPERKONDUKTOR BSCCO-2212 DAN BPSCCO-2212 AKIBAT VARIASI SUHU SINTERING MENGGUNAKAN METODE PENCAMPURAN BASAH

Risky Putra Ramadhan, 1617041028 (2021) ANALISIS PERTUMBUHAN FASE SUPERKONDUKTOR BSCCO-2212 DAN BPSCCO-2212 AKIBAT VARIASI SUHU SINTERING MENGGUNAKAN METODE PENCAMPURAN BASAH. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Rizky Ramadhan.pdf Download (223Kb) | Preview
	File PDF SKRIPSI TANPA PEMBAHASAN - Rizky Ramadhan.pdf Restricted to Hanya staf Download (1792Kb)
Preview	File PDF SKRIPSI FULL-1 - Rizky Ramadhan.pdf Download (1790Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian dilakukan untuk mengetahui pengaruh variasi suhu sintering terhadap tingkat kemurnian fase superkonduktor BSCCO-2212 dan BPSCCO-2212 menggunakan metode pencampuran basah. Variasi suhu sintering yang digunakan adalah 825, 830, 835 dan 840°C selama 20 jam. Hasil XRD menunjukkan bahwa tingkat kemurnian fase pada superkonduktor BSCCO-2212 dan BPSCCO-2212 meningkat hingga mencapai titik optimum pada suhu sintering 835°C kemudian mengalami penurunan pada suhu sintering 840°C. Fraksi volume tertinggi sampel BSCCO-2212 didapatkan pada suhu sintering 835°C sebesar 71,09% dan derajat orientasi tertinggi didapatkan pada suhu sintering 830°C sebesar 23,38%. Pada sampel BPSCCO-2212 fraksi volume tertinggi didapatkan pada suhu sintering 835°C sebesar 52,59% dan derajat orientasi tertinggi pada suhu sintering 830°C sebesar 43,49%. Hasil perbandingan sampel BSCCO-2212 dan BPSCCO-2212 diperoleh bahwa sampel BPSCCO-2212 memiliki tingkat kemurnian fase yang lebih tinggi dibandingkan BSCCO-2212. Kata kunci : Superkonduktor BSCCO-2212, Suhu Sintering, Fraksi Volume The research is done to see how variations of sintering temperatures would affect the level of chasteness of the superconducting phases of BSCCO-2212 and the BPSCCO-2212 using methods of moist mixing. Variations of sintering temperatures used are 825, 830, 835 and 840°C over 20 hours. XRD results show that the level of phase innocence on the superconductors of BSCCO-2212 and the BPSCCO-2212 increased to the point of optimum at sintering temperature 835°C then went down at sintering 840°C. The higher-volume fraction of the BSCCO- 2212 obtained at sintering temperature 835°C by 71,09% and the highest degree of orientation obtained at sintering temperature 830°C by 23.38%. On sample BPSCCO-2212 fractions of the highest volume found at sintering temperature 835°C for 52.59% and the highest degree of orientation at sintering temperature 830°C by 43.49%. The ratio of sample BSCCO-2212 and BPSCCO-2212 were obtained that sample BPSCCO-2212 had a higher level of phase purity than BSCCO-2212. Keywords: Superconductor BSCCO-2212, Sintering Temperature, Volume Fraction

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 510 Matematika
Program Studi:	FAKULTAS MIPA > Prodi Matematika
Pengguna Deposit:	AM.d Firlia Hidayah
Date Deposited:	09 Jan 2023 00:48
Terakhir diubah:	09 Jan 2023 00:48
URI:	http://digilib.unila.ac.id/id/eprint/68122

Actions (login required)

Lihat Karya Akhir