STUDI FOTODEGRADASI ZAT WARNA RHODAMIN B DENGAN SPEKTROFOTOMETRI SINAR TAMPAK MEMANFAATKAN TiO2/ZEOLIT-A SEBAGAI KATALIS

AFIFA , NABILLA MUTIQ (2022) STUDI FOTODEGRADASI ZAT WARNA RHODAMIN B DENGAN SPEKTROFOTOMETRI SINAR TAMPAK MEMANFAATKAN TiO2/ZEOLIT-A SEBAGAI KATALIS. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK.pdf Download (837Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (1293Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1292Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian fotodegradasi pewarna tekstil rhodamin B menggunakan katalis TiO2/zeolit-A. Pada awalnya katalis dibuat dengan mensintesis zeolit-A dengan silika sekam padi dan alumunium foil dengan metode hidrotermal pada suhu 100°C selama 72 jam dan dikalsinasi selama 6 jam pada suhu 550°C. Kemudian zeolit-A dikarakterisasi menggunakan instrumen XRD dan SEM. Karakterisasi XRD mengindikasikan bahwa zeolit-A dalam fasa kristal dan memiliki nilai kristalinitas sebesar 32,12%. Kemudian karakterisasi SEM menunjukkan bahwa zeolit-A memiliki morfologi permukaan berbentuk kubus. Selanjutnya zeolit-A diimpregnasi dengan TiO2 untuk mendapatkan komposit TiO2/zeolit-A dengan kadar TiO2 5, 10, dan 15% lalu dianalisis menggunakan XRF. Selanjutnya komposit digunakan sebagai katalis untuk fotodegradasi rhodamin B. Persen degradasi dihitung berdasarkan nilai absorbansi pada panjang gelombang maksimum (548 nm) yang telah diketahui dengan memindai larutan rhodamin B 50 ppm pada rentang panjang gelombang 400-800 nm menggunakan spektrofotometer UV-Vis. Selain penentuan panjang gelombang maksimum, metode juga divalidasi dan diperoleh linearitas metode dengan nilai R2 sebesar 0,9966, LoD 0,1032 ppm, LoQ 0,3447 ppm, dan %RSD sebesar 0,1981. Hasil percobaan fotodegradasi menunjukkan bahwa katalis TiO2 5%/zeolit-A memiliki persen degradasi tertinggi, yaitu 39,24% dengan waktu optimum 90 menit dan pH 5. Kata kunci: fotodegradasi, rhodamin B, zeolit-A, komposit TiO2/zeolit-A Photodegradation research has been conducted on rhodamin B textile dyes using TiO2/zeolite-A catalysts. Initially, the catalyst was made by synthesizing zeolite-A with rice husk silica and aluminum foil by hydrothermal method at 100°C for 72 hours and calcined for 6 hours at 550°C. Then zeolite-A is characterized using XRD and SEM instruments. XRD characterization indicates that zeolite-A is in the crystalline phase and has a crystallinity value of 32.12%. Then the SEM characterization showed that zeolite-A has a cube-shaped surface morphology. Zeolite-A was impregnated with TiO2 to obtain a TiO2/zeolite-A composite with TiO2 loads of 5, 10, and 15% by weight and then analyzed using XRF. The composite is used as a catalyst for photodegradation of rhodamin B. Percent degradation is calculated based on the absorbance value at the maximum wavelength (548 nm) that has been known by scanning a 50 ppm rhodamin B solution in the wavelength range of 400-800 nm using a UV-Vis spectrophotometer. In addition to the determination of the maximum wavelength, the method was also validated and obtained the linearity of the method with values of R2 of 0.9966, LoD of 0.1032 ppm, LoQ of 0.3447 ppm, and %RSD of 0.1981. The results of the photodegradation experiment showed that the 5%/zeolite-A TiO2 catalyst had the highest percent degradation, which was 39.24% with an optimum time of 90 minutes and a pH of 5. Keywords: photodegradation, rhodamine B, zeolite-A, TiO2/zeolite-A composite

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2301164298 . Digilib
Date Deposited:	30 Jan 2023 06:33
Terakhir diubah:	30 Jan 2023 06:33
URI:	http://digilib.unila.ac.id/id/eprint/68546

Actions (login required)

Lihat Karya Akhir