PENGARUH TEGANGAN ELECTROSPINNING PADA PEMBENTUKAN SERAT NANO TITANIUM DIOKSIDA (TiO2)

IRA SUDARSONO PUTRI, 2027041003 (2023) PENGARUH TEGANGAN ELECTROSPINNING PADA PEMBENTUKAN SERAT NANO TITANIUM DIOKSIDA (TiO2). Masters thesis, FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM.

[img]
Preview
File PDF
1. ABSTRAK.pdf

Download (258Kb) | Preview
[img] File PDF
2. TESIS FULL.pdf
Restricted to Hanya staf

Download (2510Kb)
[img]
Preview
File PDF
3. TESIS TANPA BAB PEMBAHASAN.pdf

Download (2511Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pembentukan serat nano TiO2 telah berhasil dibuat dengan menggunakan metode electrospinning. Penelitian ini bertujuan untuk mengetahui pengaruh variasi tegangan terhadap morfologi dan ukuran diameter serat nano TiO2. Persiapan awal untuk bahan TiO2 dilakukan menggunakan metode sol-gel. Penelitian ini menggunakan bahan titanium isopropoxide (TTIP), etanol sebagai pelarut, asam asetat sebagai katalis dan polyvinylpirolidone (PVP) sebagai polimer pembentuk serat. Variasi tegangan electrospinning yang digunakan yaitu 16, 18, 22, dan 24 kV. Proses electrospinning dilakukan pada jarak tip ke kolektor sebesar 13 cm dengan laju aliran 1,5 ml/jam dan dikalsinasi pada suhu 450 oC selama 3 jam. Hasil pengukuran viskositas TiO2/PVP diperoleh sebesar 0,2889 Pa.s dan tegangan permukaan TiO2/PVP diperoleh sebesar (29 ± 4) dyn/cm. Nilai tersebut dinyatakan sebagai nilai larutan yang dapat digunakan dalam proses electrospinning. Karakterisasi Scanning Electron Microscopy (SEM) memperlihatkan morfologi serat nano TiO2 yang relatif seragam dengan ukuran diameter serat terjadi penurunan seiring bertambahnya tegangan electrospinning dengan ukuran diameter serat berkisar antara 190-255 nm. Hasil analisis X-Ray Diffraction (XRD) memperlihatkan bahwa struktur kristal yang terbentuk pada suhu kalsinasi 450 oC yaitu fasa anatase dan ukuran kristal pada puncak tertinggi 2θ yaitu 25,37o sebesar 17,56 nm. Kata kunci: Serat nano, TiO2, Tegangan Electrospinning, PVP TiO2 nanofibers have been succesfully produced by Electrospinning Method. The purpose of this research is to find out the influence of voltage variety towards morphology, fiber diameter size and structure of TiO2 nanofibers crystal. TiO2 synthesis was done by using sol-gel method. This research used titanium isopropoxide (TTIP), ethanol as solvent, acetic acid as catalyst and polyvinylpirolidone (PVP) as polymer of fibers formation. The variety of voltage which have been used such as 16, 18,22, and 24 kV. Electrospinning process was done through the distance of tip to the collector by 13 cm with 1,5 ml/hour flow rate and was calcined at temperature of 450o C for 3 hours. The of TiO2/PVP viscosity measurement value of 0,2889 Pa.s and Nanofibers TiO2/PVP surface tension at (29 ± 4) dyn/cm. Scanning Electron Microscopy (SEM) characterization shows nanofibers morphology is relatively uniform and rather continuous with the diameter size of fibers decreases along with the increase of electrospinning voltage at fibers diameter size between 194-255 nm. X-Ray Diffraction (XRD) analysis result show that crystal peak formed on TiO2 nanofibers is anatase phase and the crystal size at the highest peak of 2θ 25,37o is 17,56 nm. Keywords : nanofibers, TiO2, Electrospinning voltage, PVP

Jenis Karya Akhir: Tesis (Masters)
Subyek: 500 ilmu pengetahuan alam dan matematika
Program Studi: FAKULTAS MIPA > Prodi Magister Ilmu Fisika
Pengguna Deposit: 2301893259 . Digilib
Date Deposited: 09 Feb 2023 08:19
Terakhir diubah: 09 Feb 2023 08:19
URI: http://digilib.unila.ac.id/id/eprint/69037

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir