PEMANFAATAN LIMBAH KULIT KAKAO SEBAGAI BAHAN PEMBUAT PORI PADA ECOPAVINGS BLOCK

Erlangga, (2023) PEMANFAATAN LIMBAH KULIT KAKAO SEBAGAI BAHAN PEMBUAT PORI PADA ECOPAVINGS BLOCK. FAKULTAS PERTANIAN, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (489Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (3857Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (3826Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Curah hujan yang tingga sepanjang tahun 2018-2019 mengakibatkan genangan air pada daerah perumahan. Hal ini diakibatkan oleh tidak terdapat daerah resapan air yang cukup, karena daerah tertutup perumahan sehingga tidak dapat meneruskan air. Sehingga dibutuhkan pembuatan paving block yang dapat menyerap air hujan ketanah. Tujuan dari penelitian ini yaitu memanfaatkan limbah Kulit Kakao untuk pembuatan eco-paving block dan menganalisis karakteristik fisik eco-paving block Kulit Kakao. Tahapan pembuatan paving block pada penelitian ini yaitu kulit kakao dipotong-potong berukuran kecil, setelah dikeringkan, dan dilakukkan pembakaran agar kulit kakao berubah menajadi arang. Setelah itu dilakukan pembuatan paving block sesuai dengan perlakuan yang sudah ditetapkan. Perlakuan pada penelitian ini terdiri dari 4 perlakuan dengan kompisisi yeng berbeda beda yaitu perlakuan 1 dengan semen + pasir 98% + 2% arang, perlakuan 2 terdapat semen + pasir 96% + 4% arang, perlakuan 3 semen + pasir 94% + 6% arang, dan perlakuan terakhir yaitu semen + pasir 92% + 8% arang. Pengaruh limbah kulit kakao diharapkan dapat meningkatkan infiltrasi terhadap Eco-Paving Blocks pada penelitian ini. Paving block limbah kulit kakao yang dihasilkan pada penelitian ini memiliki nilai uji densitas rata-rata yaitu1670,751 kg/m3 hingga 1929,642 kg/m3 . Uji resapan air didapat nilai rata rata sebesar 14,61% perlakuan satu, 11,18% perlakuan 2, 19,82% perlakuan 3, dan 15,19% perlakuan 4. Untuk uji infiltrasi didapat nilai terbesar yaitu pada perlakuan 1 yaitu 0,355 mm/s. Uji tampak diperoleh dengan bentuk tekstur paving yang sesuai di dapat pada faktor P2 dikarenakan tekstur yang dihasilkan bagus dan tidak ada celah atau cacat pada saat paving telah di cetak. Sedangkan pada uji kuat tekan didapat nilai rata-rata yang menurun secara signifikan dari variasi P1 hingga variasi P4. Nilai tertinggi perlakuan P1 dengan nilai sebesr 0,0154 MPA, sedangkan nilai terendah terjadi pada perlakuan P4 dengan nilai sebesar 0,0030 MPA. Namun pada penelitian ini ada beberapa parameter yang belum memenuhi kriteria paving standar mutu D. Kata Kunci: Eco-paving block, limbah kulit kakao High rainfall throughout 2018-2019 resulted in waterlogging in residential areas. This is due to the fact that there are not enough water catchment areas, because the area is closed to housing so that water cannot pass through. So it is necessary to make paving blocks that can absorb rainwater to the ground. The purpose of this research is to utilize cocoa shell waste to manufacture eco-paving blocks and to analyze the physical characteristics of cocoa shell eco-paving blocks. The steps for making paving blocks in this study were that the cocoa shells were cut into small pieces, after being dried, and fired so that the cocoa shells turned into charcoal. After that, paving blocks are made according to the predetermined treatment. The treatment in this study consisted of 4 treatments with different compositions, namely treatment 1 with cement + 98% sand + 2% charcoal, treatment 2 with cement + 96% sand + 4% charcoal, treatment 3 cement + 94% sand + 6% charcoal, and the last treatment is cement + 92% sand + 8% charcoal. The effect of cocoa shell waste is expected to increase infiltration of EcoPaving Blocks in this study. The paving block of cocoa shell waste produced in this study has an average density test value of 1670.751 kg/m3 to 1929.642 kg/m3. The water absorption test obtained an average value of 14.61% for treatment one, 11.18% for treatment 2, 19.82% for treatment 3, and 15.19% for treatment 4. For the infiltration test, the largest value was obtained in treatment 1, namely 0.355 mm /s. The visible test is obtained with the shape of the appropriate paving texture obtained on the P2 factor because the resulting texture is good and there are no gaps or defects when the paving has been printed. Meanwhile, in the compressive strength test, the average value decreased significantly from the P1 variation to the P4 variation. The highest value was in treatment P1 with a value of 0.0154 MPA, while the lowest value occurred in treatment P4 with a value of 0.0030 MPA. However, in this study there were several parameters that did not meet the criteria for quality standard paving D. Keywords: Eco-paving block, cocoa shell waste

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 630 Pertanian dan teknologi yang berkaitan
Program Studi:	Fakultas Pertanian dan Pascasarjana > Prodi Teknik Pertanian
Pengguna Deposit:	2301901076 . Digilib
Date Deposited:	16 Jun 2023 02:36
Terakhir diubah:	16 Jun 2023 02:36
URI:	http://digilib.unila.ac.id/id/eprint/72304

Actions (login required)

Lihat Karya Akhir