PENGARUH WAKTU PENGGUNAAN SEL VOLTA BERBAHAN ELEKTROLIT AIR LAUT TERHADAP PERMUKAAN KATODA TEMBAGA DILAPISI PERAK

NENCHY ANUGRAH BR , TARIGAN (2023) PENGARUH WAKTU PENGGUNAAN SEL VOLTA BERBAHAN ELEKTROLIT AIR LAUT TERHADAP PERMUKAAN KATODA TEMBAGA DILAPISI PERAK. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (1498Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2076Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2077Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk menganalisis pengaruh waktu penggunaan sel volta berbahan elektrolit air laut terhadap permukaan katoda tembaga dilapisi perak. Bahan yang digunakan yaitu alumina, semen, tembaga, AgNO3, air laut dan aquades. Alat yang digunakan yaitu power supply, multimeter, dan stopwatch. Penelitian ini dilakukan dengan empat tahapan, yakni preparasi bahan, pembuatan alat dan pengujian sistem, pengambilan sampel, dan karakterisasi permukaan tembaga berlapis perak serta pengolahan data hasil. Katoda tembaga dikarakterisasi menggunakan SEM-EDX. Berdasarkan hasil yang diperoleh terjadi kenaikan tegangan dan arus setelah 24 jam dan 72 jam. Kenaikan tegangan dan arus tersebut didukung oleh kenaikan massa katoda tembaga (Cu) yang bereaksi dengan air laut setelah 24 jam dan 72 jam. Nilai perhitungan hambatan dalam dipengaruhi oleh kenaikan tegangan dan arus, nilai hambatan dalam lebih kecil pada penggunaan pertama dibandingkan dengan setelah 24 jam dan 72 jam. Nilai perhitungan daya diperoleh paling besar pada 72 jam, yang dipengaruhi oleh kenaikan tegangan dan arus. Dapat disimpulkan bahwa hasil hambatan dan daya listrik katoda Cu dilapisi Ag memiliki korelasi dengan hasil karakterisasi SEM-EDX Kata Kunci : Tembaga, Perak, Air Laut, SEM-EDX, Sel Volta ABSTRACT This study was conducted to analyze the influence of time using voltaic cells with seawater electrolyte toward cathode surface silver coated copper. The materials used are aluminium oxide, cement, copper, AgNO3, seawater, and distilled water. The tools used are power supply, multimeter, and stopwatch. This research was conducted in four stages, namely material preparation, tool making and system testing, sampling, and surface characterization of silver-plated copper and processing of result data. Cathode was characterization using SEM-EDX. Based on the results obtained, there was an increase in voltage and current after 24 hours and 72 hours. The increase in voltage and current is supported by an increase in the mass of the copper cathode (Cu) which reacts with seawater after 24 hours and 72 hours. The calculated value of the internal resistance is affected by the increase in voltage and current, the value of the internal resistance is smaller in the first use compared to after 24 hours and 72 hours. The maximum power calculation value is obtained at 72 hours, which is affected by the increase in voltage and current. It can be concluded that the electrical resistance and power test results for Cu cathode coated with Ag have a correlation with the SEM-EDX characterization results Key Words : Copper, Silver, Seawater, SEM-EDX, Voltaic Cell

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2301332889 . Digilib
Date Deposited:	15 Aug 2023 08:47
Terakhir diubah:	15 Aug 2023 08:47
URI:	http://digilib.unila.ac.id/id/eprint/74804

Actions (login required)

Lihat Karya Akhir