PENGARUH VARIASI KOMPOSISI Fe DAN Ni TERHADAP PEMBENTUKAN BAHAN KATODE Na2Fe1-xNixSiO4 BERBASIS SILIKA SEKAM PADI

MONICA , CALISTA (2024) PENGARUH VARIASI KOMPOSISI Fe DAN Ni TERHADAP PEMBENTUKAN BAHAN KATODE Na2Fe1-xNixSiO4 BERBASIS SILIKA SEKAM PADI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG .

Preview	File PDF ABSTRAK.pdf Download (3773Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Bahan katode yang terbuat dari silika sekam padi, "Fe(" 〖"NO" 〗_"3" ").9" "H" _"2" "O" dan 〖"Ni(" 〖"CH" 〗_"3" "COO)" 〗_"2" ".4" "H" _"2" "O" dengan biaya relatif murah, keamanan tingkat tinggi dan ketersediaan sumber daya natrium, nikel yang melimpah. Penelitian ini dilakukan dengan tujuan mengetahui pengaruh variasi komposisi Fe dan Ni terhadap kolerasi antar gugus fungsi, morfologi, unsur penyusun dan konduktivitas listrik pada pembentukan bahan katode 〖"Na" 〗_"2" 〖"Fe" 〗_"1-x" 〖"Ni" 〗_"x" Si"O" _"4" berbasisi silika sekam padi. Pembuatan silika sekam padi dari ekstrak sekam padi KOH 5 % untuk membentuk sol silika, ditambahkan HN"O" _"3" 10 % untuk membentuk silika gel, dioven 110 ℃ untuk membentuk silika padatan, digerus untuk mendapatkan serbuk silika. Pembuatan katode menggunakan metode sol-gel, NaOH, "Fe(" 〖"NO" 〗_"3" ").9" "H" _"2" "O" , 〖"Ni(" 〖"CH" 〗_"3" "COO)" 〗_"2" "•4" "H" _"2" "O" , "C" _"6" "H" _"8" "O" _"7" "." "H" _"2" "O" dan 〖"SiO" 〗_"2" dari sekam padi digabungkan kemudian disintering 500 ℃ dengan variasi komposisi Fe : 0,98; 0,97; 0,96; 0,95 mol dan Ni: 0,02; 0,03; 0,04; 0,05 mol. Gugus fungsi terdiri dari susunan ikatan antar atom pembentuk yaitu Na-O, Fe-O, Ni-O dan Si-O. Morfologi berupa gumpalan tak seragam dengan butirannya cenderung berbentuk balok dan berdiameter kecil. Unsur penyusun yang terkandung pada bahan katode yaitu O, Na, Si, Fe dan Ni. Konduktivitas listrik sampel bahan katode 〖"Na" 〗_"2" 〖"Fe" 〗_"1-x" 〖"Ni" 〗_"x" 〖"SiO" 〗_"4" nilainya berkisar pada orde 〖"10 " 〗^"-4" hingga 〖"10 " 〗^"-3" S/m, menunjukkan bahwa bahan katode ini bersifat semikonduktor. Kata kunci : Bahan katode, Doping Ni, konduktivitas listrik, silika sekam padi. The cathode material is made from rice husk silica, "Fe(" 〖"NO" 〗_"3" ").9" "H" _"2" "O" , and 〖"Ni(" 〖"CH" 〗_"3" "COO)" 〗_"2" ".4" "H" _"2" "O" with relatively low cost, high safety, and abundant availability of sodium and nickel resources. This research aims to investigate the influence of Fe and Ni composition variations on the correlation between functional groups, morphology, constituent elements, and electrical conductivity in the formation of 〖"Na" 〗_"2" 〖"Fe" 〗_"1-x" 〖"Ni" 〗_"x" Si"O" _"4" cathode material based on rice husk silica. The process involves creating rice husk silica through a 5 % KOH extract to form silica sol, adding 10% HNO3 to create silica gel, heating at 110 ℃ to form solid silica, and grinding to obtain silica powder. The cathode is produced using the sol-gel method, combining NaOH, "Fe(" 〖"NO" 〗_"3" ").9" "H" _"2" "O" , 〖"Ni(" 〖"CH" 〗_"3" "COO)" 〗_"2" "•4" "H" _"2" "O" , "C" _"6" "H" _"8" "O" _"7" "." "H" _"2" "O" , and 〖"SiO" 〗_"2" from rice husks, followed by sintering at 500 ℃ with varying Fe and Ni compositions. Identified functional groups include Na-O, Fe-O, Ni-O, and Si-O bonding arrangements. The morphology exhibits irregular clusters with granules tending to be rectangular and small in diameter. The constituent elements contained in the cathode material are O, Na, Si, Fe and Ni. The electrical conductivity of the cathode material samples 〖"Na" 〗_"2" 〖"Fe" 〗_"1-x" 〖"Ni" 〗_"x" Si"O" _"4" values are on the order of 〖"10 " 〗^"-4" to 〖"10 " 〗^"-3" S/m, indicating that this cathode material is semiconducting. Keywords: Cathode material, Ni doping, electrical conductivity, rice husk silica.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2308654576 . Digilib
Date Deposited:	02 Feb 2024 08:19
Terakhir diubah:	02 Feb 2024 08:19
URI:	http://digilib.unila.ac.id/id/eprint/78522

Actions (login required)

Lihat Karya Akhir