NALISIS KEGAGALAN FATIGUE IMPACT UNTUK MEMAKSIMALKAN LIFETIME PELAT PEMECAH ALIRAN BATUBARA PADA SCREEN CV507 PT BUKIT ASAM PELABUHAN TARAHAN

KIAGUS , A HADI (2024) NALISIS KEGAGALAN FATIGUE IMPACT UNTUK MEMAKSIMALKAN LIFETIME PELAT PEMECAH ALIRAN BATUBARA PADA SCREEN CV507 PT BUKIT ASAM PELABUHAN TARAHAN. Masters thesis, UNIVERSITAS LAMPUNG.

	File PDF (ABSTRAK KIAGUS A HADI) open[1] Download (96Kb)
	File PDF (FILE FULL KIAGUS A HADI) open[1] Restricted to Hanya staf Download (96Kb) | Minta salinan
	File PDF (FILE FULL TANPA BAB PEMBAHASAN) open[1] Download (96Kb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pelat pemecah aliran batubara merupakan komponen dari unit Vibrating Screen CV507 berfungsi sebagai penyaring batubara dengan ukuran yang tidak sesuai produk jual di atas 50mm. Pelat ini berfungsi untuk meredam laju aliran curahan batubara yang menimbulkan impak besar dan kerusakan di area vibrating screen. Namun dalam operasionalnya pelat pemecah aliran batubara sering mengalami kerusakan pelat patah akibat impak dari curahan batubara yang cukup tinggi 5meter dalam kurun waktu 2 minggu sampai dengan 1 bulan sehingga menganggu jam operasional. Total waktu halangan tahun 2022-2023 yaitu 695 menit. Penilitian ini bertujuan menganalisis kegagalan fatigue impact dengan mengetahui maximum stress equivalent, total deformation, dan jumlah siklus pada pelat pemecah aliran batubara serta menentukan material yang mempunyai life time yang panjang untuk dijadikan pelat pemecah aliran batubara. Metode yang digunakan yaitu Studi Literatur (analisa beban, momentum, tekanan impak, analisa karakteristik fatigue dari material), Observasi (analisa beban operasional) dan Finite Element Analysis. Beban impak operasional maksimal yang didapatkan adalah 1,5ton atau gaya 15kN. Hasil dari penelitian ini didapat bahwa tegangan maksimum Von Mises paling tinggi adalah material ST37 tebal 15mm dengan nilai 2463,1 MPa, dan paling rendah adalah material GS20Mn tebal 20mm dengan nilai 1306,9 MPa. Nilai deformasi total paling tinggi adalah ST52 tebal 15mm dengan nilai13,305mm dan yang paling rendah adalah material ST52 tebal 20mm dengan nilai 10,693mm. Umur pakai paling tinggi adalah material ST52 tebal 20mm dengan nilai 96.348 siklus dan paling rendah adalah material Hardock HB400 tebal 15mm dengan nilai 74.572 siklus. Kata kunci : pelat pemecah aliran batubara, fatigue impact, stress equivalent, total deformation ABSTRACT FATIGUE IMPACT FAILURE ANALYSIS TO MAXIMIZE THE LIFETIME OF COAL FLOW BREAKER PLATE ON SCREEN CV507 PT BUKIT ASAM PORT TARAHAN By Kiagus A Hadi, Asnawi Lubis, Jamiatul Akmal The coal flow breaker plate is a component of the CV507 vibrating screen unit that functions as a coal filter with a size that does not match the selling product over 50mm. The purpose of this plate is to reduce the flow rate of coal bulk load, which causes great impact and damage in the vibrating screen area. However, in its operation, the coal flow breaker plate often experiences broken plate damage due to the impact of coal outflow which is quite high at 5m within a period of 2 weeks to 1 month, thus disrupting the operating hours. The total hitch time in 2022-2023 is 695 minutes. This research aims to analyze the fatigue impact failure by knowing the maximum stress equivalent, total deformation and number of cycles on the coal flow breaker plate and to determine the material that has long life to be used as coal flow breaker plate. The methods used are literature study (analysis of load, moment, impact pressure, analysis of fatigue characteristics of the material), observation (operational load analysis) and finite element analysis. The maximum operational impact load obtained is 1.5ton or 15kN force. The results of this study showed that the highest maximum Von Mises stress was for 15mm thick ST37 material with a value of 2463,1 MPa, and the lowest was for 20mm thick GS20Mn material with a value of 1306,9 MPa. The highest total deformation value is for 15mm thick ST52 with a value of 13.305mm, and the lowest is for 20mm thick ST52 material with a value of 10.693mm. The highest fatigue life is for 20mm thick ST52 material with a value of 98,438 cycles and the lowest is for15mm thick Hardock HB400 material with a value of 74.572 cycles. Keywords: coal flow breaker plate, fatigue impact, stress equivalent, total deformation

Jenis Karya Akhir:	Tesis (Masters)
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan 600 Teknologi (ilmu terapan) > 670 Manufaktur, pabrik-pabrik
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Desi Zulfi Melasari
Date Deposited:	28 Jan 2025 12:51
Terakhir diubah:	28 Jan 2025 12:51
URI:	http://digilib.unila.ac.id/id/eprint/81586