STUDI PENAMBAHAN EKSTRAK BUAH MENGKUDU (Morinda citrifolia) DAN ASAP CAIR CANGKANG KELAPA SAWIT SEBAGAI INHIBITOR KERAK KALSIUM SULFAT (CaSO4) MENGGUNAKAN METODE SEEDED EXPERIMENT

Az zahra , Joanda (2025) STUDI PENAMBAHAN EKSTRAK BUAH MENGKUDU (Morinda citrifolia) DAN ASAP CAIR CANGKANG KELAPA SAWIT SEBAGAI INHIBITOR KERAK KALSIUM SULFAT (CaSO4) MENGGUNAKAN METODE SEEDED EXPERIMENT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK AZ ZAHRA JOANDA - Azzahra Joandha.pdf Download (284Kb) | Preview
	File PDF SKRIPSI FULL AZ ZAHRA JOANDA - Azzahra Joandha.pdf Restricted to Hanya staf Download (4014Kb) | Minta salinan
Preview	File PDF SKRIPSI FULL TANPA BAB PEMBAHASAN AZ ZAHRA JOANDA - Azzahra Joandha.pdf Download (3904Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pada proses peindustrian, saluran pipa air dapat menimbulkan adanya pembentukan kerak. Potensi kerak salah satunya disebabkan oleh garam CaSO4 yang ditemukan dalam hampir semua jenis saluran air sehingga menyebabkan terganggunya aliran akibat pengecilan diameter pipa dan menghambat aliran fluida pada sistem pipa tersebut. Oleh karena itu, dalam penelitian ini telah dilakukan pengujian inhibitor campuran ekstrak mengkudu dan asap cair cangkang kelapa sawit (MA) pada kerak kalsium sulfat (CaSO4) menggunakan metode seeded experiment pada variasi konsentrasi larutan pertumbuhan CaSO4 sebesar 0,0250; 0,0375; 0,0500; dan 0,0675 M yang diujikan pada variasi perbandingan konsentrasi inhibitor MA 1:5, 3:5, 5:5, dan 7:5. Efektivitas tertinggi terjadi pada konsentrasi larutan pertumbuhan CaSO4 0,0250 M dengan perbandingan konsentrasi inhibitor campuran MA 7:5 diperoleh persentase sebesar 155,46 %. Berdasarkan hasil analisis kualitatif menggunakan Scanning Electron Microscopy (SEM) dan X-Ray Difraction (XRD) menunjukkan bahwa kerak CaSO4 tanpa penambahan inhibitor seperti batang menumpuk dengan ukuran besar dan panjang yang terdiri dari fasa gipsum dan basanit, sedangkan setelah penambahan inhibitor permukaan kristal lebih pendek, tidak merata, dan rapuh yang terdiri dari fasa gipsum dan basanit dengan intensitas menurun, serta muncul fasa baru anhidrit. Analisis kuantitatif menggunakan Particle Size Analyzer (PSA) menunjukkan bahwa kerak CaSO4 sebelum dan setelah penambahan inhibitor mengalami penurunan ukuran kristal yakni nilai rata-rata (mean) dari 123,29 μm menjadi 109,81 μm dan nilai tengah (median) dari 104,14 μm menjadi 43,14 μm. Sehingga inhibitor campuran MA dapat digunakan sebagai penghambat kerak CaSO4. Kata Kunci: asap cair cangkang kelapa sawit, ekstrak mengkudu, CaSO4, kerak, inhibitor In industrial processes, water pipes can cause scale formation. One of the potential scales is caused by CaSO4 salts which are found in almost all types of water pipes, causing flow disruption due to reducing pipe diameters and inhibiting fluid flow in the pipe system. Due to these problems, this research was carried out by testing the inhibitor mixture of noni extract and palm oil shell liquid smoke (MA) was tested on calcium sulfate (CaSO4) scale using the seeded experiment method at varying concentrations of the CaSO4 growth solution of 0.0250; 0.0375; 0.0500; and 0.0675 M tested at various rations of MA inhibitor concentrations of 1:5, 3:5, 5:5, and 7:5. The highest effectiveness occurred at the concentration of 0.0250 M CaSO4 growth solution with a ratio of 7:5 mixture inhibitor MA concentration, yielded the effectiveness percentage value of 155.46 %. Based on the results of qualitative analysis using Scanning Electron Microscopy (SEM) and X-Ray Difraction (XRD), showed that the CaSO4 scale without the addition of inhibitors such as rods that were piled, large-sized, and elongted consisting of gypsum and basanite phases, while after the addition of inhibitors, the crystal surface looked shorter, smaller size and fragile consisting of gypsum and basanite phases with decreased intensity, and a new anhydrite phase appears. Quantitative analysis using the Particle Size Analyzer (PSA) showed that the CaSO4 scale after the addition, the inhibitors had decreased the crystal size with the average value (mean) from 123.29 μm to 109.81 μm and the middle value (median) from 104.14 μm to 43.14 μm. In conclusion, the mixture inhibitor (MA) can be used to overcome CaSO4 scale inhibitors. Keywords: palm oil shell liquid smoke, noni extract, CaSO4, scale, inhibitors

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia
Pengguna Deposit:	UPT . Siswanti
Date Deposited:	27 Oct 2025 08:51
Terakhir diubah:	27 Oct 2025 08:51
URI:	http://digilib.unila.ac.id/id/eprint/92103

Actions (login required)

Lihat Karya Akhir