PENGARUH KONSENTRASI TiO2 TERHADAP PERMITIVITAS GREEN- SYNTHESIZED Fe3O4/TiO2

Onesimus , Putry Philia Saragih (2025) PENGARUH KONSENTRASI TiO2 TERHADAP PERMITIVITAS GREEN- SYNTHESIZED Fe3O4/TiO2. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK NEW - Onesimus Saragih.pdf Download (2659Kb) | Preview
	File PDF SKRIPSI FULL NEW - Onesimus Saragih.pdf Restricted to Hanya staf Download (4011Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN NEW - Onesimus Saragih.pdf Download (4009Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Telah dilakukan penelitian mengenai pengaruh konsentrasi TiO2 terhadap permitivitas Fe3O4/TiO2 yang disintesis menggunakan metode green-synthesized dengan ekstrak Moringa oleifera (MO) sebagai agen reduktor alami. Variasi rasio Fe3O4 terhadap TiO2 (1:0 ; 1:3 ; 1:5 dan 1:7) digunakan untuk mengevaluasi perubahan sifat dielektrik material yang dihasilkan. Karakterisasi dilakukan pengukuran permitivittas dielektrik riil dan imajiner, loss tangent, serta impedansi dalam rentang frekuensi 10 kHz hingga 900 kHz. Hasil penelitian menunjukkan bahwa peningkatan konsentrasi TiO2 berkontribusi terhadap peningkatan permitivitas dielektrik pada frekuensi rendah, sedangkan pada frekuensi tinggi nilainnya cenderung stabil. Selain itu, nilai impedansi mengalami penurunan pada frekuensi rendah dan meningkat kembali pada frekuensi tinggi, yang mengindikasikan adanya interaksi antara Fe3O4 danTiO2. Kata Kunci: Fe3O4/TiO2, green-synthesis, permitivitas dielektrik, impedansi, loss tangent. A study has been conducted on the effect of TiO2 concentration on the permittivity of Fe3O4/TiO2 synthesized using the green-synthesis method with Moringa Oleifera (MO) extract as a natural reducing agent. The Fe3O4 toTiO2 ratio variations (1:0 ; 1:3 ; 1:5 dan 1:7) were used to evalute changes in the dielectric properties of the resulting material. Characterization was carried out by measuring real and imaginary dielectric permittivity, loss tangent, and impedance within the frequency range of 10 kHz to 900 kHz. The results showed that an increase in TiO2 concentration contributed to the enhancement of dielectric permittivity at low frequencies, while at high frequencies, its value tended to remain stable. Additionlly, the impedance values decreased at low frequencies and increased again at high frequencies, indicating an interaction between Fe3O4 andTiO2 Keywords: Fe3O4/TiO2, green-synthesis, dielectric permittivity, impedance, loss tanget.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 530 Fisika
Program Studi:	FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Fisika
Pengguna Deposit:	A.Md Cahya Anima Putra .
Date Deposited:	28 Jan 2026 11:27
Terakhir diubah:	28 Jan 2026 11:27
URI:	http://digilib.unila.ac.id/id/eprint/95155

Actions (login required)

Lihat Karya Akhir