SINTESIS DAN KARAKTERISASI POLIPADUAN POLI ASAM LAKTAT DENGAN POLIKAPROLAKTON SEBAGAI BAHAN BAKU BENANG BEDAH OPERASI

FRANSISCA CLODINA DACASTA, 1417011045 (2018) SINTESIS DAN KARAKTERISASI POLIPADUAN POLI ASAM LAKTAT DENGAN POLIKAPROLAKTON SEBAGAI BAHAN BAKU BENANG BEDAH OPERASI. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
Text
ABSTRAK.pdf

Download (260Kb) | Preview
[img] Text
SKRIPSI FULL.pdf
Restricted to Registered users only

Download (4Mb)
[img]
Preview
Text
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (4Mb) | Preview

Abstrak

Penelitian tentang penggunaan polimer biodegradable dan bioresorbable banyak dilakukan baik dalam bentuk homopolimer atau polipaduan. Penelitian ini banyak berfokus pada pengembangan bahan-bahan baru yang digunakan pada bidang lanjutan seperti aplikasi biomedis, contohnya benang bedah. Pada penelitian ini dibuat polipaduan antara polimer poli asam laktat dan polikaprolakton dengan 3 perbandingan berbeda untuk mengetahui kompisisi polipaduan yang cocok sebagai benang bedah. Sintesis yang dilakukan diantaranya PAL: PCL (4:1 (A4B)), PAL: PCL (1:1(A1B)), dan PAL: PCL (1:4(AB4)). Setelah disintesis, dilakukan uji degradasi dan uji kekuatan mekanik untuk mengetahui komposisi polipaduan yang terbaik sebagai benang bedah. Diantara ketiga polipaduan yang dibuat, polipaduan A4B memiliki presentase penurunan berat terbesar yaitu 2,39% pada larutan NaCl 0,9%, 1,75% pada larutan buffer fosfat pH 6, 2,84% pada buffer fosfat pH 7, dan 4,53% pada buffer fosfat pH 8. Nilai kekuatan mekanik terbesar juga dimiliki polipaduan A4B sebesar 18 N/mm2, namun hasil ini masih cukup jauh jika dibandingkan dengan nilai kekuatan mekanik benang bedah komersial. Penyebab rendahnya nilai kekuatan mekanik ditunjukkan oleh karakterisasi FTIR, TGA/DTA dan SEM. Karakterisasi FTIR menunjukkan tidak adanya interaksi kimia antara PAL dan PCL yang dipadukan, dibuktikan dengan munculnya spektrum-spektrum yang sama antara PAL dan PCL sebelum dan sesudah dipadukan. Homogenitas yang kurang antara PAL dan PCL juga menjadi penyebab rendahnya kekuatan mekanik pada polipaduan A4B. Hal ini dibuktikan dengan nilai stabilitas termal polipaduan A4B yang rendah dan morfologi acak jika dibandingkan antara polipaduan A4B dengan PAL atau PCL yang murni. Kata kunci: Polimer, Poli asam laktat (PAL), Polikaprolakton (PCL), Benang bedah SYNTHESIS AND CHARACTERIZATION POLYBLEND OF POLY LACTIC ACID WITH POLYCAPROLACTONE AS RAW MATERIAL OF SURGICAL Research about the use of biodegradable and bioresorbable polymers is mostly carried out in the form of homopolymers or polyblends. This research focuses about developing new materials such as biomedical applications of surgical. In this study a combination of poly lactic acid (PLA) polymers and polycaprolactone (PCL) was made with 3 different comparisons to determine the polyblend composition suitable as a surgical. The syntheses carried out include PLA: PCL (4: 1 (A4B)), PLA: PCL (1:1 (A1B)), and PLA: PCL (1:4 (AB4)). After being synthesized, the degradation test and mechanical strength test were carried out to find out the best polyblend composition as a surgical. Among the three polyblend made, A4B had the largest presentation of weight loss of 2,39% in 0,9% NaCl solution, 1,75% in pH 6 phosphate buffer solution, 2,84% in pH 7 phosphate buffer, and 4,53% in pH 8 phosphate buffer. The value of the largest mechanical strength also has A4B polyblend of 18 N/mm2, but this result is still quite far compared to the value of the mechanical strength of commercial surgical threads. The cause of the low mechanical strength is indicated by the characteristics of FTIR, TGA/DTA and SEM. FTIR characterization showed no chemical interaction between PLA and PCL combined, it showed by of the same spectra between PLA and PCL before and after integration. The lack of homogeneity between PLA and PCL is also a cause of low mechanical strength in A4B polyblend. This is showed by the low thermal stability value of A4B polyblend and random morphology when compared between pure A4B polymers and pure PLA or PCL. Keyword: Polymer, Poly Lactic Acid (PLA), Polycaprolatcone (PCL), Surgical

Tipe Karya Ilmiah: Skripsi
Subyek: Q Science (General) > Q Science (General)
Q Science (General) > QD Chemistry
Program Studi: Fakultas MIPA > Prodi Kimia
Depositing User: 188439274 . Digilib
Date Deposited: 18 Dec 2018 07:29
Last Modified: 18 Dec 2018 07:29
URI: http://digilib.unila.ac.id/id/eprint/54767

Actions (login required)

View Item View Item