PENGARUH UKURAN SERBUK LOGAM HASIL PEMESINAN TERHADAP KUALITAS SINTERING MAGNESIUM AZ31 UNTUK APLIKASI BAUT TULANG

SUEF SUPRIYADI , 1215021072 (2017) PENGARUH UKURAN SERBUK LOGAM HASIL PEMESINAN TERHADAP KUALITAS SINTERING MAGNESIUM AZ31 UNTUK APLIKASI BAUT TULANG. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (6Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1775Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1775Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Magnesium AZ31 Memiliki potensi sebagai implan pengganti bagian tubuh dari manusia karena memiliki kecocokan pada tubuh manusia magnesium bersifat biokopatibilitas. Porositas dan densitas menentukan hasil dari proses sintering, yang dilakukan dengan fariasi ukuran serbuk 56 μm, 100 μm, 200 μm, dan 250 μm. yang diharapkan implan dari magnesium AZ31 dapat luruh dalam tubuh. Pemanasan yang dilakukan didalam furnace dengan temperatur 450º ditahan selama 45 menit kemudian didinginkan pada temperatur ruang dan kompaksi dengan tekanan 300 psi selama 5 menit proses sintering menggunakan gas argon untuk melindungi spesimen. Untuk mendapatkan data pada pengujianya dilakukan pengujian metalografi mikroskop optik, SEM EDX dan kekerasan Vickers Kata kunci : Biomaterial, Mampu luruh, Fariasi, Bikompabilitas, Temperature, Sintering. ABSTRACT Magnesium (Mg) AZ31 has the potential as an implant replacement for parts of human bone because it has suitability with human body parts, magnesium is biocompatibility. On the sinter process with powders size variation 56, 100, 200 dan 250 μmmagnesium (Mg) AZ31 can be dissolved in human body without being toxic. Heating was done in a furnace with a temperature of 450ºC and holding time 45 minutes then cooled with room temperature and compaction at 300 psi for 5 minutes sintering process used argon gas to protect specimen from getting burn. In this research, it is known that the smaller size of the powder will make the greatest hardness like powder size 250μm with hardness value 43 Hardness Vickers (HV) and powder size 56μm is 63 HV. Keywords: Biomaterial, Dissolve, Variation, Biocompatibility, Temperature, Sintering.

Jenis Karya Akhir:	Skripsi
Subyek:	> Mesin (General). Mesin Sipil (General) > Mesin (General). Mesin Sipil (General) Mesin (General). Mesin Sipil (General)
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	68695311 . Digilib
Date Deposited:	06 Dec 2017 08:39
Terakhir diubah:	06 Dec 2017 08:39
URI:	http://digilib.unila.ac.id/id/eprint/29172

Actions (login required)

Lihat Karya Akhir