PENGARUH PENGUAT FLY ASH DAN KARBON HITAM TERHADAP SIFAT KERAMIK KAOLIN UNTUK MATERIAL PELAPIS PIPA BAJA PENYALUR LIMBAH FLY ASH

heljefri, 1725021004 (2021) PENGARUH PENGUAT FLY ASH DAN KARBON HITAM TERHADAP SIFAT KERAMIK KAOLIN UNTUK MATERIAL PELAPIS PIPA BAJA PENYALUR LIMBAH FLY ASH. Other thesis, UNIVERSITAS LAMPUNG.

Preview	File PDF file abstrak tesis - UPK BAM Engineering.pdf Download (4Mb) | Preview
	File PDF tesis full_heljefri 17_ref 2 tesis tanpa lampiran isi 2 - UPK BAM Engineering.pdf Restricted to Hanya staf Download (6Mb)
Preview	File PDF tesis full_heljefri 17_ref 2 tesis tanpa bab pembahasan 2 - UPK BAM Engineering.pdf Download (6Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

PLTU Bukit Asam Tanjung Enim, merupakan pembangkit listrik berbahan bakar batubara dengan kapasitas 4 x 65 MW, membutuhkan bahan bakar 25.000 ton per hari. Dalam pengelolaannya, PLTU menghasilkan limbah padat dan cair yang dihasilkan per hari. Salah satu limbah padat yang tidak dapat diolah adalah fly ash, dimana fly ash yang dihasilkan sebesar 7% atau 20 ton per hari. Sehingga penggunaan fly ash sebagai media pelapis pipa fly ash. Pada penelitian ini dilakukan pengujian pengaruh ukuran fly ash dan serbuk karbon hitam yang dikombinasikan dengan serbuk kaolin sebagai bahan penguat terhadap kualitas slury transport pipe coating produk keramik. Serbuk fly ash dibuat dalam ukuran serbuk yang dicampur (acak) dengan serbuk karbon hitam, dan serbuk kaolin dengan ukuran 74 m (200 mesh). Serbuk campuran tersebut kemudian dikemas dengan tekanan 20 ton selama 5 menit untuk menghasilkan body yang berwarna hijau segar. Kemudian dipanaskan dengan tungku, pada suhu 800 oC selama 2 jam. Pengujian fisik yang dilakukan adalah pengujian porositas, densitas, dan ketahanan panas. Pengujian mekanis yang dilakukan adalah pengujian ketahanan aus dan pengujian kekerasan. Hasil pengujian menunjukkan keausan tertinggi pada KC 90 dan KF 50, sedangkan nilai kekerasan tertinggi pada KCF 50 dan KF 50. Kata kunci: komposit keramic matric, slury transport pipe coating ceramics PLTU Bukit Asam Tanjung Enim, is a coal-fired power plant with a capacity of 4 x 65MW, requiring 25,000 tons of fuel per day. In its management, PLTU produces solid and liquid waste which is produced per day. One of the solid wastes that cannot be processed is fly ash, where the fly ash produced is 7% or 20 tons per day. So that the use of fly ash as a medium for coating fly ash pipes. In this study, the effect of the sizeof fly ash and carbon black powder combined with kaolin powder as a reinforcing material was tested on the quality of the slury transport pipe coating ceramic products.Fly ash powder was prepared in powder sizes mixed (random) with carbon black powder, and kaolin powder with a size of 74 μm (200 mesh). The mixed powder is then packed with a pressure of 20 tons for 5 minutes to produce a crisp green body. Then heated with a furnace, at a temperature of 800 oC for 2 hours. Physical testing conducted is testing of porosity, density, and heat resistance. The mechanical tests carried out are wearresistance testing and hardnesstesting. The test resultsshowed thehighest wear at KC 90 and KF 50, while the highest hardness values were at KCF 50 and KF 50. Key words: composite keramic matric, slury transport pipe coating ceramics

Jenis Karya Akhir:	Tesis (Other)
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi Magister Teknik Mesin
Pengguna Deposit:	UPT . Meda Sulistiana
Date Deposited:	27 May 2022 08:54
Terakhir diubah:	27 May 2022 08:54
URI:	http://digilib.unila.ac.id/id/eprint/61975

Actions (login required)

Lihat Karya Akhir