KARAKTERISTIK PERAMBATAN RETAK FATIK PIPA BAJA TYPE API 5L PSL -1 GRADE B

TRI , KUSUMA WARDANI (2024) KARAKTERISTIK PERAMBATAN RETAK FATIK PIPA BAJA TYPE API 5L PSL -1 GRADE B. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK - Tri Kusumawardani.pdf Download (247Kb) | Preview
	File PDF SKRIPSI FULL - Tri Kusumawardani.pdf Restricted to Hanya staf Download (3025Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN - Tri Kusumawardani.pdf Download (1531Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pipa baja API 5L Grade B merupakan pipa yang digunakan dalam transportasi minyak bumi dan gas alam. Tujuan dari penelitian ini adalah untuk mengetahui karakteristik perambatan retak fatik pada material pipa baja API 5L-B. Uji tarik (ASTM 8) dan uji perambatan retak fatik (ASTM E647) menggunakan spesimen Compact Tension (CT). Parameter pengujian yang digunakan dalam penelitian ini yaitu Pmax = 3,566 kN, Pmin = 0,357 kN, σyield = 399.251 MPa dan f = 10 Hz. Pengukuran panjang retak menggunakan metode compliance serta data panjang retak dan jumlah siklus dianalisis menggunakan metode polynomial incremental untuk menentukan laju perambatan retak fatik (da/dN) dan faktor intensitas tegangan (ΔK). Plot data da/dN vs ΔK dilakukan untuk menentukan koefisien persamaan Paris pada daerah perambatan retak stabil-stage II. Nilai konstanta m = 3,607 dan nilai konstanta C = 1,176x10-12 . Pengamatan mikrostruktur material menggunakan mikroskop optik menunjukkan fasa ferit dan perlit. Pengamatan SEM pada permukaan patahan menunjukkan pola patahan intergranular. Selain itu, permukaan patahan menunjukkan adanya garis striasi, secondary crack dan voids. Kata Kunci : Pipa baja API 5L grade B, Perambatan retak fatik, Mikrostruktur, Fraktografi iv ABSTRACT FATIGUE CRACK PROPAGATION CHARACTERISTICS OF TYPE API 5L PSL -1 GRADE B STEEL PIPE By TRI KUSUMA WARDANI API 5L Grade B steel pipe is a pipe used in the transportation of petroleum and natural gas. The purpose of this study is to determine the characteristics of fatigue crack propagation in API 5L-B steel pipe material. Tensile test (ASTM 8) and fatigue crack propagation test (ASTM E647) using Compact Tension (CT) specimens. The parameters used during the test were Pmax = 3,566 kN, Pmin = 0,357 kN, σyield = 399.251 MPa and f = 10 Hz. Crack length measurements using the compliance method and data on crack length and number of cycles were analyzed using the incremental polynomial method to determine the fatigue crack propagation rate (da/dN) and stress intensity factor (ΔK). A plot of da/dN vs ΔK data was performed to determine the coefficients of the Paris equation in the stable-stage II crack propagation region. The constant value m = 3,607 and the constant value C = 1,176x10-12 . Microstructural observations of the material using optical microscopy showed ferrite and pearlite phases. SEM observation of the fracture surface showed an intergranular fracture pattern. In addition, the fracture surface showed the presence of striation lines, secondary cracks and voids. Key words : API 5L grade B steel pipe, Fatigue crack propagation, Microstructure, Fractograf

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi Magister Teknik Mesin
Pengguna Deposit:	UPT . Desi Zulfi Melasari
Date Deposited:	14 Feb 2025 02:06
Terakhir diubah:	14 Feb 2025 02:06
URI:	http://digilib.unila.ac.id/id/eprint/83706

Actions (login required)

Lihat Karya Akhir