STUDI PENAMBAHAN CAMPURAN EKSTRAK KEMENYAN, GAMBIR, DAN ASAP CAIR CANGKANG KELAPA SAWIT SEBAGAI INHIBITOR KERAK KALSIUM KARBONAT (CaCO3)

Zuanita , Maharani (2025) STUDI PENAMBAHAN CAMPURAN EKSTRAK KEMENYAN, GAMBIR, DAN ASAP CAIR CANGKANG KELAPA SAWIT SEBAGAI INHIBITOR KERAK KALSIUM KARBONAT (CaCO3). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
1. ABSTRAK - ABSTRACT - Zuanita Maharani.pdf

Download (201Kb) | Preview
[img] File PDF
2. SKRIPSI FULL - Zuanita Maharani.pdf
Restricted to Hanya staf

Download (2824Kb) | Minta salinan
[img]
Preview
File PDF
3. SKRIPSI TANPA BAB PEMBAHASAN - Zuanita Maharani.pdf

Download (1929Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Kerak kalsium karbonat (CaCO3) merupakan masalah utama dalam sistem perpipaan industri karena dapat mengurangi efisiensi operasional. Penelitian ini bertujuan untuk mempelajari pengaruh dan efektivitas campuran ekstrak kemenyan, gambir, dan asap cair cangkang kelapa sawit sebagai inhibitor kerak CaCO3 serta menentukan komposisi campuran inhibitor terbaik. Penelitian ini menggunakan metode seeded experiment dengan konsentrasi larutan pertumbuhan CaCO3 yang digunakan yaitu 0,025; 0,0375; 0,050; dan 0,0625 M, dan dengan perbandingan konsentrasi inhibitor ekstrak kemenyan dan asap cair cangkang kelapa sawit dibuat tetap yakni 50 dan 250 ppm sedangkan pada ekstrak gambir dibuat bervariasi yakni 100, 150, 200, 250, dan 300 ppm. Penambahan inhibitor pada larutan pertumbuhan 0,025 M dengan perbandingan konsentrasi campuran inhibitor terbaik yakni 1:6:5 menghasilkan efektivitas sebesar 63,19%. Hasil karakterisasi menggunakan Scanning Electron Microscope dan X-Ray Diffraction menunjukkan adanya perubahan morfologi kristal CaCO3, pada kerak tanpa penambahan inhibitor terdapat fasa kalsit dan aragonit, dan setelah penambahan inhibitor terdapat adanya fasa baru yaitu fasa vaterit yang mudah larut dalam air sehingga mudah dihilangkan. Distribusi ukuran partikel kerak CaCO3 menggunakan Particle Size Analyzer menunjukkan adanya penurunan ukuran partikel kerak CaCO3, sebelum menggunakan inhibitor dengan nilai rata-rata yaitu 70,92 μm kemudian turun menjadi 64,3 μm setelah penambahan inhibitor. Kata kunci: kemenyan, gambir, asap cair cangkang kelapa sawit, kalsium karbonat, inhibitor Calcium carbonate (CaCO3) scale is a major problem in industrial piping systems because it can reduce operational efficiency. This research aims to examine effectiveness of a mixture of frankincense and gambier extract, and palm shell liquid smoke as a CaCO3 scale inhibitor and to determine the best composition of the inhibitor. This research used a seeded experiment method with CaCO3 growth solution concentrations of 0,025; 0,0375; 0,050; and 0,0625 M, and the concentration ratio of the inhibitor extract of frankincense and liquid smoke from palm kernel shells was kept constant at 50 and 250 ppm, while the gambir extract was varied at 100, 150, 200, 250, and 300 ppm. The addition of inhibitor to 0,025 M growth solution with an inhibitor ratio of 1:6:5 had the best effectiveness of 63.19%.The results of characterization using Scanning Electron Microscope, and X-Ray Diffraction show a change in the morphology of CaCO3 crystals, there are calcite and aragonite phases before using inhibitors and after using inhibitors there is a new phase, namely the vaterite phase which is easily soluble in water, so it is easy to remove. The particle size distribution of CaCO3 using Particle Size Analyzer shows a decrease, particle size distribution before using the inhibitor with an average value of 70,92 μm to 64,3 μm after the addition of the inhibitor. Keywords: frankincense, gambier, palm shell liquid smoke, calcium carbonate, inhibitor

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia
Pengguna Deposit: . . Yulianti
Date Deposited: 17 Oct 2025 01:27
Terakhir diubah: 17 Oct 2025 01:27
URI: http://digilib.unila.ac.id/id/eprint/91345

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir